Abstract:The skeletal Ni P amorphous alloy(Raney Ni P) was prepared by alkali leaching a Ni P Al amorphous alloy obtained by the rapid quenching technique. Its amorphous structure was confirmed by both the XRD and EXAFS. By using liquid phase benzene hydrogenation, an important reaction in industrial production, the selectivity to cyclohexane and the catalytic activity(including hydrogen uptake rate, reaction conversion and TOF value) of the as prepared Raney Ni P catalyst were measured. In comparison with the corresponding Ni P amorphous alloy obtained via the traditional rapid quenching technique, the crystallized Raney Ni P, and Raney Ni which was widely used in industry, the Raney Ni P catalyst exhibited much higher activity besides the perfect selectivity to cyclohexane. The DSC analysis also revealed its high thermal stability. These results demonstrated its potential application in industrial processes. By measuring the effects of the benzene concentration, the hydrogen pressure, and the reaction temperature on the hydrogenation rate, the reaction kinetics and the apparent activation energies were determined, based on which, a plausible mechanism was proposed. The higher activity of Raney Ni P than that of traditional Ni P was mainly due to its higher surface area. While the higher activity of Raney Ni P than that of Raney Ni was mainly attributed to the nature of the active sites. Since no significant electronic interaction between Ni and P in Ni P amorphous alloy was found by XPS spectra, the geometric effect was considered as the main promoting effect, which was briefly discussed according to various characterizations, such as ICP, XRD, EXAFS, BET, and hydrogen chemisorption. The crystallization deactivation of Raney Ni P amorphous alloy was attributed to the change in both the surface area and the structure of the active sites.

A study on the Raney nickel catalysts prepared from Ni-Fe-Al alloys

Metals Leaching Mechanism of Fe or/and Mo Modified Raney-Ni Catalysts and Their Catalytic Hydrogenation of Glucose

Acid-Resistant Performance of Ni-Based Hydrogenation Catalysts Supported by Hydrophobic Activated Carbon

Influence of Mo Modified Raney Nion Liquid Catalytical Hydrogenation of 2,4-Difluoronitrobenzene

Microcalorimetric studies of Raney nickel catalysts

Catalytic Decomposition of N,N-dimethylformamide over Raney Ni Catalysts Modified with Sn

Preparation of novel Raney-Ni catalysts and characterization by XRD, SEM and XPS

Xrd, Sem and Edax Studies of the Preparation Process of Novel Raney-Ni Catalyst

Effect of support texture properties on Ni-Fe/γ-Al_2O_3 catalyst structure and catalytic performance for CO methanation

XRD and XPS Studies on the Ultra‐uniform Raney‐Ni Catalyst Prepared from the Melt‐quenching Alloy

Preparation of Raney Ni Catalyst and Research on Its Catalytic Hydrogenation Performance for Alkenyl Aromatics

Research, Development, and Application of Amorphous Nickel Alloy Catalysts Prepared by Melt-Quenching

Preparation and Characterization of Bulk and Supported NiB Amorphous Alloy Catalysts with Different Particle Sizes

Effect of Preparation Process on Compressive Strength and Hydrogenation Performance of Raney-Ni/Al2o3 Catalyst

Preparation of skeletal Ni-P amorphous alloy and the study of its catalytic properties during benzene hydrogenation

General Preparation for Pt-Based Alloy Nanoporous Nanoparticles As Potential Nanocatalysts

Modification of Nickel-Based Catalyst with Transition Metals to Tailor Reaction Intermediates and Property of Coke in Steam Reforming of Acetic Acid

Catalytic Performance of Iron Oxide Loaded on Electron-Rich Surfaces of Carbon Nitride

Carbon deposition on iron-nickel alloy particles

Stoichiometric‐Ratio‐Controlled Fe and Ni Non‐noble Metal Catalysts Supported on γ‐Al2O3 for Turquoise Hydrogen and Carbon Nanotubes Production

Effect of adding nickel to iron–alumina catalysts on the morphology of as-grown carbon nanotubes