Abstract:Catalytic ammonia borane (AB) hydrolysis using supported Ni catalysts is a cost-effective way for H 2 production. However, constructing highly active Ni catalysts is still challenging due to the low intrinsic activity and easy aggregation of Ni particles at high Ni content. In this study, Ni particles in SBA-15 ( mi -Ni@SBA-15) were prepared using the template-assisted melt infiltration method. For comparison, Ni catalysts supported on SBA-15 were also prepared using conventional impregnation ( imp -Ni/SBA-15-NT) and melt infiltration method ( mi - Ni/SBA-15-NT). The catalysts were fully characterized and catalytic AB hydrolysis was carried out on the catalysts. The results showed that for imp - Ni/SBA-15-NT and mi -Ni/SBA-15-NT large Ni agglomerates were obviously observed and the mesopores of SBA-15 were partially blocked due to the formation of rodlike Ni particles. In contrast, for mi -Ni@SBA-15 the combination of the steric effect of template and tunable mesopore size of SBA-15 enables SBA-15 to effectively confine the Ni particles in its mesopores and regulate the particle size of Ni respectively. Increasing Ni content from 7.7 to 24.5 wt% only led to denser Ni particles in SBA-15 without marked growth of Ni particles for mi -Ni@SBA-15. The well-dispersed Ni particles on mi -Ni@SBA-15 with Ni content of 24.5 wt% enriched the active sites on the catalyst surface , thus leading to high catalytic activity for AB hydrolysis with a TOF of 37.8 mol H2 mol Ni −1 min −1 , which was at least 3.9 times higher than those of other tested catalysts. A comparison of the normalized catalytic activities by exposed Ni sites of catalysts with varied Ni particle sizes suggested that Ni sites on small Ni particles are more active than those on large ones. This work highlighted that mi -Ni@SBA-15 prepared using the template-assisted melt infiltration method are highly active catalysts for H 2 production from AB hydrolysis.

Preparation and Characterization of Bulk and Supported NiB Amorphous Alloy Catalysts with Different Particle Sizes

Liquid-Phase Hydrogenation of Nitrobenzene over Ag-Ni Bimetallic Catalysts Prepared by Adsorption Phase Synthesis

Effect of TiO2 Support on the Composition, Morphology and Catalytic Property of the NiB Amorphous Alloy Catalyst

Preparations,Structures and Properties of Amorphous Ni-P Alloy Catalysts

Self-assembly of mesoporous Ni–B amorphous alloy catalysts

Research, Development, and Application of Amorphous Nickel Alloy Catalysts Prepared by Melt-Quenching

NiCu Bimetallic Nanoparticles on Silica Support for Catalytic Hydrolysis of Ammonia Borane: Composition-Dependent Activity and Support Size Effect

Size-tunable Ni particles confined in the ordered mesoporous silica for catalytic H 2 production from ammonia borane hydrolysis

Two-Step, Oxygen-Free Conversion of Methane over Supported NiB Amorphous Alloy Catalysts

Self-assembly of Mesoporous Ni–P Nanosphere Catalyst with Uniform Size and Enhanced Catalytic Activity in Nitrobenzene Hydrogenation

Local Structure and Catalytic Performance of Ultrafine NiB Amorphous Alloy

Xps Studies On Surface Electronic Characteristics Of Ni-B And Ni-P Amorphous Alloy And Its Correlation To Their Catalytic Properties

Partial Hydrogenation of Cyclopentadiene over Amorphous NiB Alloy on Α-Alumina and Titania‐modified Α-Alumina

Mesoporous silica-supported NiB amorphous alloy catalysts for selective hydrogenation of 2-ethylanthraquinone

Characterization and catalytic behavior of amorphous Ni-B/AC catalysts prepared in different impregnation sequences

Low-Temperature Solution-Phase Synthesis of NiAu Alloy Nanoparticles Via Butyllithium Reduction: Influences of Synthesis Details and Application As the Precursor to Active Au-NiO/SiO2 Catalysts Through Proper Pretreatment

Amorphous Ni-B hollow spheres synthesized by controlled organization of Ni-B nanoparticles over PS beads via surface seeding/electroless plating

NiCuBimetallic Nanoparticles on Silica Support forCatalytic Hydrolysis of Ammonia Borane: Composition-Dependent Activityand Support Size Effect

Preparation of the Ni-B Amorphous Alloys with Variable Boron Content and Its Correlation to the Hydrogenation Activity

CO Methanation over Ni/SiO2 Catalyst Prepared by Ammonia Impregnation and Plasma Decomposition

The Crystallization Process and the Hydrogenation Activity of Ni-P/SiO2 Catalyst