Abstract:Catalytic ammonia borane (AB) hydrolysis using supported Ni catalysts is a cost-effective way for H 2 production. However, constructing highly active Ni catalysts is still challenging due to the low intrinsic activity and easy aggregation of Ni particles at high Ni content. In this study, Ni particles in SBA-15 ( mi -Ni@SBA-15) were prepared using the template-assisted melt infiltration method. For comparison, Ni catalysts supported on SBA-15 were also prepared using conventional impregnation ( imp -Ni/SBA-15-NT) and melt infiltration method ( mi - Ni/SBA-15-NT). The catalysts were fully characterized and catalytic AB hydrolysis was carried out on the catalysts. The results showed that for imp - Ni/SBA-15-NT and mi -Ni/SBA-15-NT large Ni agglomerates were obviously observed and the mesopores of SBA-15 were partially blocked due to the formation of rodlike Ni particles. In contrast, for mi -Ni@SBA-15 the combination of the steric effect of template and tunable mesopore size of SBA-15 enables SBA-15 to effectively confine the Ni particles in its mesopores and regulate the particle size of Ni respectively. Increasing Ni content from 7.7 to 24.5 wt% only led to denser Ni particles in SBA-15 without marked growth of Ni particles for mi -Ni@SBA-15. The well-dispersed Ni particles on mi -Ni@SBA-15 with Ni content of 24.5 wt% enriched the active sites on the catalyst surface , thus leading to high catalytic activity for AB hydrolysis with a TOF of 37.8 mol H2 mol Ni −1 min −1 , which was at least 3.9 times higher than those of other tested catalysts. A comparison of the normalized catalytic activities by exposed Ni sites of catalysts with varied Ni particle sizes suggested that Ni sites on small Ni particles are more active than those on large ones. This work highlighted that mi -Ni@SBA-15 prepared using the template-assisted melt infiltration method are highly active catalysts for H 2 production from AB hydrolysis.

NiCuBimetallic Nanoparticles on Silica Support forCatalytic Hydrolysis of Ammonia Borane: Composition-Dependent Activityand Support Size Effect

NiCu Bimetallic Nanoparticles on Silica Support for Catalytic Hydrolysis of Ammonia Borane: Composition-Dependent Activity and Support Size Effect

Liquid-Phase Hydrogenation of Nitrobenzene over Ag-Ni Bimetallic Catalysts Prepared by Adsorption Phase Synthesis

Bimetallic Au-Ni Nanoparticles Embedded in SiO2 Nanospheres: Synergetic Catalysis in Hydrolytic Dehydrogenation of Ammonia Borane.

CuNi Nanoparticles Assembled on Graphene for Catalytic Methanolysis of Ammonia Borane and Hydrogenation of Nitro/Nitrile Compounds

Non-noble Trimetallic Cu-Ni-Co Nanoparticles Supported on Metal-Organic Frameworks As Highly Efficient Catalysts for Hydrolysis of Ammonia Borane

Co-Cu nanoparticles uniformly embedded in the intra-crystalline mesoporous Silicalite-1 for catalytic ammonia borane hydrolysis

Construction of cost-effective bimetallic nanoparticles on titanium carbides as a superb catalyst for promoting hydrolysis of ammonia borane

Synthesis of Mesoporous Silica-Supported NiCo Bimetallic Nanocatalysts and Their Enhanced Catalytic Hydrogenation Performance

Monodisperse PtCu Alloy Nanoparticles As Highly Efficient Catalysts for the Hydrolytic Dehydrogenation of Ammonia Borane

Silica Confinement for Stable and Magnetic Co‐Cu Alloy Nanoparticles in Nitrogen‐Doped Carbon for Enhanced Hydrogen Evolution

Electronic Engineering Induced Ultrafine Non-Noble Nanoparticles for High-Performance Hydrogen Evolution from Ammonia Borane Hydrolysis

Ultrafine and Well-Dispersed Nickel Nanoparticles with Hierarchical Structure for Catalytically Breaking a Boron–Hydrogen Bond

Aerosol Spray Drying Guided Synthesis of Ultrasmall Alloyed Bimetallic Nanoparticles Supported on Silica for Catalytic Semihydrogenation

Preparation and Characterization of Bulk and Supported NiB Amorphous Alloy Catalysts with Different Particle Sizes

Ratio-controlled Synthesis of CuNi Octahedra and Nanocubes with Enhanced Catalytic Activity.

Size-tunable Ni particles confined in the ordered mesoporous silica for catalytic H 2 production from ammonia borane hydrolysis

Facile Synthesis of Highly Dispersed and Well‐Alloyed Bimetallic Nanoparticles on Oxide Support

Heterostructured Ni/NiO Nanoparticles on 1D Porous MoO x for Hydrolysis of Ammonia Borane

Exposed Facet Tailoring of Ni/Cu Catalysts for Boosting Dehydrogenation of Ammonia Borane

Heterostructured Ni/NiO Nanoparticles on 1D Porous MoOx for Hydrolysis of Ammonia Borane