Abstract:For the conventional Ni/SiO2 catalyst, it is a challenge to address the sintering problem of Ni particles, especially at high Ni loading. A series of Ni-phyllosilicate catalysts were prepared through the hydrothermal reaction of mesoporous SiO2 nanorods (SRs) and nickel nitrate, followed by an impregnation modification of CeO2. Hydrothermal temperature played an important role in the formation of nickel phyllosilicate. A small amount of Ni-phyllosilicate with a Ni content of 18.56 or 23.88 wt % was formed at a low hydrothermal temperature of 120 or 160 degrees C, and a large amount of nanosheet-like Ni-phyllosilicate with the Ni content as high as 31.65 wt % was obtained at a high hydrothermal temperature of 200 degrees C. The prepared Niphyllosilicate catalysts were beneficial to obtain Ni particles with small sizes (3.3-6.3 nm), even though they were reduced at 750 degrees C and possessed high Ni loadings (18.56-31.65 wt %) owing to the surface and interface confinement of nickel phyllosilicate. After the modification of CeO2 using an impregnation method, the CeO2 promoter could further reduce the Ni particle size and increase hydrogen and carbon dioxide uptakes. The CeO2-modified Niphyllosilicate catalyst (NPS-180-5C) was the best catalyst in this work, which could reach the thermodynamic equilibrium of CO methanation above 350 degrees C and exhibited high catalytic activity for CO2 methanation. In addition, for the 55 degrees C-100 h-lifetime test for CO2 methanation and 600 degrees C-6h-100% steam treatment tests, NPS-180-5C also showed an excellent antisintering property and higher hydrothermal stability than the impregnated one (N/SR-Im) owing to its special structure and confinement effect as well as promotion of CeO2 species. In all, the CeO2-modified SR-derived Ni-phyllosilicate catalyst could not only effectively suppress the problem of easy sintering of metallic Ni particles on the conventional Ni/SiO2 catalysts but also exhibit high catalytic activity and hydrothermal stability, which was a promising catalyst for both CO2 and CO methanation reactions.

CO Methanation over Ni/SiO2 Catalyst Prepared by Ammonia Impregnation and Plasma Decomposition

Effect of support texture properties on Ni-Fe/γ-Al_2O_3 catalyst structure and catalytic performance for CO methanation

Combustion-impregnation preparation of Ni/SiO2 catalyst with improved low-temperature activity for CO2 methanation

Enhanced stability of Ni/SiO2 catalyst for CO2 methanation: Derived from nickel phyllosilicate with strong metal-support interactions

Highly Dispersed Nickel Within Mesochannels of SBA-15 for CO Methanation with Enhanced Activity and Excellent Thermostability

Plasma‐Catalytic CO2 Methanation Over Supported Ni–Co Catalysts Prepared by Solution Combustion Synthesis

Impact of preparation method on nickel speciation and methane dry reforming performance of Ni/SiO2 catalysts

Insights into the Zn Promoter for Improvement of Ni/SiO 2 Catalysts Prepared by the Ammonia Evaporation Method toward CO 2 Methanation

Highly Efficient Ni-Phyllosilicate Catalyst with Surface and Interface Confinement for CO<sub>2</sub> and CO Methanation

Development of Highly Stable Ni-Al 2 O 3 Catalysts for CO Methanation

Preparation of Ni-Co/SiO2 catalyst by ammonia reflux impregnation and its CH4-CO2 reforming reaction performance

Highly active Ni/Al2O3 catalyst for CO2 methanation by the decomposition of Ni-MOF@Al2O3 precursor via cold plasma

An active and stable nickel-based catalyst with embedment structure for CO2 methanation

CO2 Methanation over CoNi Bimetal-Doped Ordered Mesoporous Al2O3 Catalysts with Enhanced Low-Temperature Activities

Nickel Phyllosilicate Derived Ni/Sio2 Catalysts For Co2 Methanation: Identifying Effect Of Silanol Group Concentration

Synthesis of Highly-Dispersed Ni/Mesoporous Silica Via an Ammonia Evaporation Method for Dry Reforming of Methane: Effect of the Ni Loadings

CO2 methanation over Co Ni bimetal-doped ordered mesoporous Al2O3 catalysts with enhanced low-temperature activities

Carbon Dioxide Reforming of Methane over Ni Supported SiO2: Influence of the Preparation Method on the Resulting Structural Properties and Catalytic Activity

Structural effect of Ni/TiO2 on CO methanation: improved activity and enhanced stability

Ammonia Decomposition over SiO2-supported Ni–Co Bimetallic Catalyst for COx-free Hydrogen Generation

Catalytic Performance for CO Methanation over Ni/MCM-41 Catalyst in a Slurry-Bed Reactor