Abstract:The objective of this study was to investigate the effect of Mo content on the catalytic properties of Mo-NiB nanoclusters in the hydrogenation of p-chloronitrobenzene. A series of Mo-doped NiB nanoalloy catalysts with various Mo contents were prepared by chemical reduction method. An excess amount of NaBH4 was used (B/Ni atomic ratio = 3) to fully reduce Ni. Even adding a small amount of Mo on NiB had a significant effect on the activity and selectivity to p-chloroaniline. The catalyst with the atomic ratio of Mo/Ni = 0.4 had the highest activity and selectivity to p-chloroaniline. The particle size of Mo-NiB decreased with an increase of Mo content, indicating that the molybdenum species suppressed the growth of the crystalline structure of NiB and helped the NiB nanocluster maintain its amorphous state. Mo-NiB formed a nanoalloy, and no discrete phase was found. High-resolution transmission electron microscopy (HRTEM) images confirmed that the shape of Mo-NiB was spherical and the particle size was in the range of 3-5 nm. The effect of molybdenum on the catalytic performance of the amorphous NiB catalysts was 2-fold. Molybdenum not only acted as a spacer but also donated partial electron to Ni. Since the -NO2 was more electronegative than -Cl, -NO2 was supposed to occupy the active site on the Ni catalytic surface at the start of the reaction. -NO2 adsorbed on the catalyst surface is hydrogenated to form p-eerie ammonium nitrate (p-CAN), which was further desorbed. Therefore, the selectivity of p-CAN would increase as the Mo contents increased. It should be noticed the overdose of Mo would cover the active sites and decreased the activity. In addition, oxygen was even more electronegative, and alloying B could engage the oxygen to activate the polar -NO2 group of p-CNB. The -NH2 of p-CAN might adsorb on the surface, alloying B and coordinating with each other. Hence, it would improve the selectivity of p-CAN by depressing the dehalogenation reaction.

Influence of Mo Modified Raney Nion Liquid Catalytical Hydrogenation of 2,4-Difluoronitrobenzene

Metals Leaching Mechanism of Fe or/and Mo Modified Raney-Ni Catalysts and Their Catalytic Hydrogenation of Glucose

Study on the Ni Supported Catalysts Used for Hydrogenation of IPN to Produce MXDA

Deactivation and Regeneration of Raney-Ni Catalyst During Multiphase Dehydrogenation of Cyclohexane

Acid-Resistant Performance of Ni-Based Hydrogenation Catalysts Supported by Hydrophobic Activated Carbon

Liquid-Phase Hydrogenation of Nitrobenzene over Ag-Ni Bimetallic Catalysts Prepared by Adsorption Phase Synthesis

Hydrogenation of P-Chloronitrobenzene on Mo-Doped NiB Cluster Catalysts

Hydrogenation Of P-Chloronitrobenzene Over Mo-Modified Nicob Nanoalloy Catalysts: Effect Of Mo Content

Liquid-phase hydrogenation of m-chloronitrobenzene over Ni-M-P amorphous alloy catalyst

Study on Silica Supported Cu Cr Mo Nitrobenzene Hydrogenation Catalysts

MoO x regulating Ni-based catalyst anchored on N-doped carbon microspheres for catalytic hydrogenation of nitroarenes

Nanostructured Ni-MoCx: An efficient non-noble metal catalyst for the chemoselective hydrogenation of nitroaromatics

Preparation of novel Raney-Ni catalysts and characterization by XRD, SEM and XPS

Effect of Mo on the Structure and Catalytic Behavior of the Rapidly Quenched Skeletal Ni-Mo Catalysts

Synthesis of Ni/Mo/N Catalyst and Its Application in Benzene Hydrogenation in the Presence of Thiophene

Influence of Ni on the active phase and hydrodenitrogenation and hydrodesulfurization activities of MoS2 catalysts

Hydrogenation of p-chloronitrobenzene on Mo, La, Fe, and W-modified NiCoB nanoalloy catalysts

Bimetallic Platinum-Tin Nanoparticles On Hydrogenated Molybdenum Oxide For The Selective Hydrogenation Of Functionalized Nitroarenes

A study on the Raney nickel catalysts prepared from Ni-Fe-Al alloys

Effect of Preparation Process on Compressive Strength and Hydrogenation Performance of Raney-Ni/Al2o3 Catalyst

A Study on the Role of Ni Atoms in the HDN Activity of NiMoS2/Al2O3 Catalyst