Effect of Lithium to Zirconium Ratio on Microstructure and Electrochemical Performances of LZO Modified LiNi0.8Co0.1Mn0.1O2 Cathode Materials
Xiaoxiao Lu,Qinzhong Mao,Yinfeng Wang,Tongzong Ji,Yunhui Zeng,Yuankang Xu,Yang Xia,RuiHao Shan,Panpan Xu,Yurong Cai,Juming Yao
DOI: https://doi.org/10.1016/j.surfin.2022.102480
IF: 6.2
2022-01-01
Surfaces and Interfaces
Abstract:Lithium zirconate (LZO) coatings were routinely applied to NCM cathode materials in industry to improve cyclability and stability, but their working principles remain some elusive. Li/Zr molar ratios for coating preparation in sol-gel route always shows random variations in literature, due to vaporization of lithium source, solid-state diffusion of Zr4+ and formation of residue lithium. In this work, LZO coatings were prepared via a sol-gel route, and chemical compositions and amounts of Zr4+ doping were studied with varying Li/Zr molar ratios. It was found that, the surface composition of LZO was dominated by Li2ZrO3 at a low Li/Zr molar ratio of 2.1, and then Li6Zr2O7 and residue lithium increased with a rising Li/Zr molar ratio. As for the ion doping, Zr4+ preferred to enter crystal lattices of NCM811 at a low Li/Zr molar ratio. The best electrochemical performance was achieved for the LZO modified NCM811 with a Li/Zr ratio of 2.4 (NCM811-LZO2.4), and the reasons could be attribute to modification processes introduced moderate Zr4+ doping and the multiphase LZO (Li2ZrO3 and Li6Zr2O7) coating onto the NCM811, which reduced the surface residue lithium and enhanced transport rate of charge carriers. As a result, the NCM811-LZO2.4 delivers a high coulombic efficiency of 91.4% in the initial cycle, outstanding capacity retention after 500 cycles (193 mAh g−1 at 0.2 C), and a good rate capacity of 155.9 mAh g−1 at 10 C. This work provides a method of tailoring chemical compositions of LZO protective coatings to improve the electrochemical performance of NCM811 materials.