Surface-Modified Quaternary Layered Ni-Rich Cathode Materials by Li 2 ZrO 3 for Improved Electrochemical Performance for High-Power Li-Ion Batteries
Juliya Jeyakumar,Yi-Shiuan Wu,She-Huang Wu,Rajan Jose,Chun-Chen Yang
DOI: https://doi.org/10.1021/acsaem.2c00224
IF: 6.4
2022-04-06
ACS Applied Energy Materials
Abstract:Quaternary Ni-rich layered cathodes are one of the most intriguing yet challenging next-generation cathode materials, and their high Ni content has made it difficult to obtain long-term cyclability. In this paper, we report the improved electrochemical performance of high-power long-life Ni-rich layered cathode materials (LiNi0.90Co0.04Mn0.03Al0.03O2, denoted NCMA), synthesized in a Couette–Taylor reactor, after depositing a homogeneous surface coating of Li2ZrO3 (LZO). Morphological analyses revealed that the thickness of the LZO coating was approximately 2.5 nm and spread uniformly on the NCMA surface. X-ray photoelectron spectroscopy indicated that the content of Li residues on the surface had greatly decreased after coating with LZO. The electrochemical performance of the coated samples was greater than that of the bare NCMA; in particular, the 1 wt % LZO-coated cathode material had a capacity retention of 90.2% after 100 cycles at 1C (vs 74.6% for the bare NCMA). Electrochemical impedance spectroscopy (EIS), cyclic voltammetry (CV), and the galvanostatic intermittent titration technique (GITT) indicated that the coating agent acted as a bridge that lowered the activation energy and polarization potential for a better Li+ ion transport. The polarization potential also decreased significantly after coating with LZO, leading to improved electrochemical kinetics. Postmortem studies after long cycling confirmed that the LZO coating layer enhanced the structural stability of the cathode.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.2c00224.Details on the schematic diagram representing the synthesis method of NCMA hydroxides and oxides, XRD patterns of bare NCMA and 5 wt % LZO-coated NCMA, peaks that correspond to LZO, XPS spectra of Co 2p, Mn 2p, and wide scan spectra of bare and 1 wt % LZO-coated NCMA cathodes, high-rate discharge plots (0.2–10C) of bare and LZO-coated NCMA cathodes, and long cycle testing of all the prepared cathodes at 1C for 100 cycles in 2.8–4.5 V (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels