Abstract:With the development of electric vehicles (EVs) and hybrid electric vehicles (HEVs), the demand for lithium ion power batteries with high energy density and long cycle life has continuously increased in the recent years. According to the "Made in China 2025" plan, the energy densities of lithium ion batteries need to reach 300 Wh.kg(-1) in 2020. Due to their high discharge capacities and work voltages, Ni-rich layered materials have attracted considerable attention from the science and industry fields as one of the most promising cathodes to achieve high energy density. According to previous reports, the discharge capacities of Ni-rich cathodes were positively correlated to their Ni content. However, the increased Ni content can aggravate the side reactions between the cathode and electrolyte, induce O loss, and trigger structural transformation from the surface to bulk. In this study, ZrO2 was coated on LiNi0.8Co0.1Mn0.1O2 with a simple wet chemical method to improve its cycle performance. The scanning electron microscopy (SEM) with energy dispersive spectroscopy (EDS) demonstrated that Zr was only detected in the ZrO2-coated samples and was mainly distributed at the surface of the secondary particles of the LiNi0.8Co0.1Mn0.1O2 cathodes. The X-ray diffraction (XRD) indicated that Zr4+ in ZrO2 migrated into the layered surface structure of LiNi0.8Co0.1Mn0.1O2 based on the shift of the (003) peak to a lower angle, which was considered as a lattice expansion along the c axis. Under the cut-off voltage of 4.3 and 4.5 V, the capacity retentions of the LiNi0.8Co0.1Mn0.1O2 cathodes improved from 84.89 to 97.61% and 75.60 to 81.37%, respectively, after 100 cycles at 1C. This was mainly attributed to the doped Zr4+ in surface structure as opposed to the ZrO2 coating. The X-ray photoelectron spectroscopy (XPS) indicated that the Ni3+ at the surface of LiNi0.8Co0.1Mn0.1O2 was reduced to Ni2+ after the Zr4+ surface doping due to charge balance. Rietveld refinement also indicated that the Li+/Ni2+ cation disordering improved after the Zr4+ in ZrO2 doped into NCM surface structure. The raised cation disordering may be triggered by the increased content of Ni2+ and their migration into Li layers due to the similar ion radius of Li+ (0.076 nm) and Ni2+ (0.069 nm). A structure-reconstructed layer at the surface of LiNi0.8Co0.1Mn0.1O2 was formed after the Zr4+ doping, which had been confirmed by transmission electron microscope (TEM). It was determined that this structure-reconstructed layer can hinder the side reactions at the interface and stabilize the bulk structure during cycles; thus, the cycle stability of LiNi0.8Co0.1Mn0.1O2 material was improved.

Enhanced electrochemical properties and thermal stability of Zr4+ doped Li1.20Mn0.54Ni0.13Co0.13O2 cathode material by a Li ion conductor of Li3PO4 surface coating

Preparation and Electrochemical Properties of Li[Ni1/3Co1/3Mn1−x/3Zrx/3]O2 Cathode Materials for Li-ion Batteries

Enhanced electrochemical performance of Li 1.2 Mn 0.54 Ni 0.13 Co 0.13 O 2 cathode material coated with Li + -conductive Li 2 SiO 3 for lithium ion batteries

Improved Li-ion Diffusion and Stability of a LiNi0.5Mn1.5O4 Cathode Through in Situ Co-Doping with Dual-Metal Cations and Incorporation of a Superionic Conductor

Effects of ZrO2 Coating on Ni-rich LiNi0.8Co0.1Mn0.1O2 Cathodes with Enhanced Cycle Stabilities

Investigation of Li 3 PO 4 Coating and Nb 5+ Doping Effect on the Crystal Structure and Electrochemical Properties of Ni-Rich LiNi 0.85 Co 0.05 Mn 0.10 O 2 Cathode

Sufficient utilization of Zr4+ on improving the structure and surface property of the Ni-rich cathode materials for lithium ion batteries.

Enhanced Electrochemical Performance of Li3PO4 Modified Li[Ni0.8Co0.1Mn0.1]O2 Cathode Material Via Lithium-Reactive Coating

Enhanced Electrochemical Properties of Zr4+-doped Li1.20[Mn0.52Ni0.20Co0.08]O2 Cathode Material for Lithium-ion Battery at Elevated Temperature

Improved Electrochemical Performance and Thermal Stability of Li-Excess Li1.18co0.15ni0.15mn0.52o2 Cathode Material by Li3po4 Surface Coating

ZrO 2 Coating of LiNi 1/3 Co 1/3 Mn 1/3 O 2 Cathode Materials for Li-ion Batteries

Cycle performance improvement of Li-rich layered cathode material Li[Li0.2Mn0.54Ni0.13Co0.13]O2 by ZrO2 coating

Li2ZrO3 Coating and Poly(3,4-ethylenedioxythiophene) Encapsulating on Li[Li0.2Mn0.54Ni0.13Co0.13]O2 with the Stabilized Structure Interface Layer As Cathode Material

Improvement in the Electrochemical Performance of LiNi0.8Co0.1Mn0.1O2 Cathode Material by Li2ZrO3 Coating

Amorphous Li2ZrO3 nanoparticles coating Li[Li0·17Mn0·58Ni0.25]O2 cathode material for enhanced rate and cyclic performance in lithium ion storage

Effect of ZnO modification on the performance of LiNi0.5Co0.25Mn0.25O2 cathode material

Improved Electrochemical Performance of Li1.2Mn0.54Ni0.13Co0.13O2 Cathode Material Coated with Ultrathin ZnO

Boosting cell performance of LiNi0.8Co0.1Mn0.1O2 cathode material via structure design

Synergistic effects of Zr doping and Li2ZrO3/WO3 co-coating on the physicochemical and electrochemical properties of cobalt-free LiNi0.8Mn0.2O2

Effects of Li2TiO3 Coating on the Structure and the Electrochemical Properties of LiNi0.5Mn0.5O2 Cathode Materials at High Voltages

Improving electrochemical performances of Lithium-rich oxide by cooperatively doping Cr and coating Li3PO4 as cathode material for Lithium-ion batteries