Li 2 ZrO 3 Coating and Poly(3,4-ethylenedioxythiophene) Encapsulating on Li[Li 0.2 Mn 0.54 Ni 0.13 Co 0.13 ]O 2 with the Stabilized Structure Interface Layer as cathode material

Tingrui Liu,Meng Zhang,Min Zhu,Zeru Du,Wenyu Wang,Yue Wang,Chun Xia,Feng Chen

DOI: https://doi.org/10.1149/1945-7111/ab9eeb

IF: 3.9

2020-07-06

Journal of The Electrochemical Society

Abstract:The wide application of Manganese-rich cathode materials have been severely restricted by the large initial irreversible capacity loss, poor cycling stability and low discharge capability at high rate. To ameliorate these severe challenges, the Li₂ZrO₃ and PEDOT materials were adopted to synthesize the Li₂ZrO₃ and PEDOT co-coated cathode by the sol-gel method with a calcination process. The SEM and TEM images revealed the Li₂ZrO₃ and PEDOT were uniformly covered on the surface of Li[Li_0.2Mn_0.54Ni_0.13Co_0.13]O₂. The electrochemical properties of cathode were obviously enhanced by the Li₂ZrO₃ coating and PEDOT coating. The Li₂ZrO₃ coated cathode, PEDOT coated cathode and Li₂ZrO₃/PEDOT coated cathode respectively delivered the discharge capacities of 120.5, 113.5 and 128.6 mAhg⁻¹, much higher than that (82.3 mAhg⁻¹) of Li[Li_0.2Mn_0.54Ni_0.13Co_0.13]O₂. Besides, the pristine cathode merely retained a capacity of 156.7 mAhg⁻¹ after 300 cycles at 45 °C. While a large discharge capacity of 201.4 mAh g⁻¹ and a supernal capacity retention of 90.8% were acquired for Li₂ZrO₃/PEDOT coated cathode after 300 cycles. The electrochemical impedance spectroscopy (EIS) measurement implied the Li₂ZrO₃ coating and PEDOT coating layer could repress the growth of the charge transfer resistance and accelerate the Li⁺ diffusion during cycling.

electrochemistry,materials science, coatings & films