Synthesis of LiNi0.9Co0.05Mn0.05O2 and modification with co-doping of Zr4+ and W6+ using acid leaching solution from spent lithium-ion batteries

Rui Zhu,Guanghui Guo,Tian Zhou,Yanjiang Chen,Yan Yang

DOI: https://doi.org/10.1007/s11581-024-05856-z

IF: 2.961

2024-10-01

Ionics

Abstract:Considering the increase in raw material prices and environmental pollution, the spent lithium-ion battery cathode material was leached with oxalic acid and sulfuric acid, and LiNi 0.9 Co 0.05 Mn 0.05 O 2 (NCM955) was prepared from the leaching solution. Then, the Ni-rich cathode material NCM955 was doped with ZrO 2 and WO 3 . The co-doping of Zr 4+ and W 6+ in Ni-rich NCM955 cathode exhibits exceptional cycle stability performance. Specifically, the Zr 4+ and W 6+ co-doped sample demonstrates a remarkable capacity retention improvement of 89.21% at 0.5 C after 100 cycles compared to the pristine sample (69.15%). Meanwhile, at a high rate of 5 C, the co-doped sample shows a significantly higher specific capacity of 125.37 mAh·g −1 compared to the pristine sample's value of only 63.98 mAh·g −1 . The results of XRD, XPS, and SEM indicate that the co-doping of Zr 4+ and W 6+ can enhance the stability of the material. Electrochemical impedance spectroscopy (EIS) results show that the co-doping of Zr 4+ and W 6+ effectively reduces the electrochemical impedance, and galvanostatic intermittent titration technique (GITT) shows that the co-doping of Zr 4+ and W 6+ increases the diffusion rate of Li + . Therefore, dual doping modification with Zr 4+ and W 6+ is beneficial for enhancing both structural stability and electrochemical performance of Ni-rich layered oxide cathode materials.

chemistry, physical,physics, condensed matter,electrochemistry