Bifunctional Surface Coating of LiAlO 2 /Si 1– x Al x O 2 Hybrid Layer on Ni-Rich Cathode Materials for High Performance Lithium-Ion Batteries
Hongqiang Wang,Youqi Chu,Qichang Pan,Chunlei Tan,Ying Shi,Yan Li,Sijiang Hu,Fenghua Zheng,Youguo Huang,Qingyu Li
DOI: https://doi.org/10.1021/acssuschemeng.1c01028
2021-06-25
Abstract:As a candidate material for high energy density cathode, nickel-rich layered oxide cathode material LiNi<sub>0.6</sub>Co<sub>0.2</sub>Mn<sub>0.2</sub>O<sub>2</sub> has become the current research hotspot for lithium-ion batteries. However, the instability of the surface reaction interface promotes the change of surface structure and bulk structure for LiNi<sub>0.6</sub>Co<sub>0.2</sub>Mn<sub>0.2</sub>O<sub>2</sub>, resulting in poor cycling stability that hindered its practical application. Here, the LiNi<sub>0.6</sub>Co<sub>0.2</sub>Mn<sub>0.2</sub>O<sub>2</sub> surface modified by hybrid coating layer () is reported. In this constructed hybrid layer, the LiAlO<sub>2</sub> with layered structure can be firmly anchored on the NCM surface, and Si<sub>1–<i>x</i></sub>Al<sub><i>x</i></sub>O<sub>2</sub> with high electrical conductivity and chemical stability can be used as a protective layer to inhibit the occurrence of surface side reactions. Hence, combining the advantages of the LiAlO<sub>2</sub> and Si<sub>1–<i>x</i></sub>Al<sub><i>x</i></sub>O<sub>2</sub> coating layer, which can effectively suppress the structural transformation and surface reaction interface failure upon long cycling, thus has improved the electrochemical performance accordingly. As a result, LiAlO<sub>2</sub>/Si<sub>1–<i>x</i></sub>Al<sub><i>x</i></sub>O<sub>2</sub> surface-modified LiNi<sub>0.6</sub>Co<sub>0.2</sub>Mn<sub>0.2</sub>O<sub>2</sub> exhibits excellent rate performance, with a high discharge specific capacity of 153.4 mAh/g even at 10 C. In addition, the cyclic stability is also much improved, which can deliver a high discharge capacity of 130.1 mAh/g after 500 cycles at 5 C, with a capacity retention of 78.5%.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.1c01028?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.1c01028</a>.In situ XRD assembly drawing; TG–DSC–DTG curves of LiOH/γ-AlOOH and LiOH/SiO<sub>2</sub>; XRD patterns of α-LiAlO<sub>2</sub> and Li<sub>2</sub>SiO<sub>3</sub>; XRD patterns of NCM, , , AlO(OH), SiO<sub>2</sub>, and ; SEM and EDS mapping images of NCM before and after washing; XPS spectra of NCM after washing; HRTEM images of NCM and ; XPS spectra of Co 2p and Mn 2p taken from the surface of NCM, , and samples; electrical conductivity; ICP-OES quantification results of samples; electrochemical performance at 1 and 5 C; electrochemical properties of our work and other literature about NCMs; CV curves; CV curves at various scan rates; Nyquist plots; electrochemical resistance; XRD patterns before and after 500 cycles at 5 C; SEM images after 500 cycles; and XPS spectra of Li 1s, P 2p, F 1s, and O 1s at the surface after 500 cycles at 5 C (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.1c01028/suppl_file/sc1c01028_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology