Cycling Stability of 5V LiMn1.5Ni0.5O4 Spinel Particles Coated with a Thin Film Mixed Conductor

Yoongu Kim,Miaofang Chi,Chengdu Liang,Nancy Dudney

DOI: https://doi.org/10.1149/ma2011-02/12/639

2011-01-01

ECS Meeting Abstracts

Abstract:Hybrid electric vehicle (HEV) and plug-in hybrid electric vehicle (PHEV) require high power energy sources which are inexpensive and safe. Among various battery materials, 5V LiMn1.5Ni0.5O4 spinel materials are especially of interests for these vehicle applications because of their high operating voltage of ~4.7V and because manganese is inexpensive and less toxic than Ni and Co. However, the cycle life of these cathodes is inadequate and elevated temperature cycling cause rapid loss of capacity of the LiMn1.5Ni0.5O4 cells. This capacity degradation can be attributed to dissolution of Mn and Ni elements, solid electrolyte interphase (SEI) formation and electrolyte decomposition with high-voltage cycling [1]. Metal oxide coatings, which are usually synthesized by solution-based coating techniques, have improved capacity retention of the LiMn1.5Ni0.5O4 cells at the elevated temperatures and have been usually synthesized by solution-based coating techniques [2,3]. Recently, we have successfully coated nanometer thick amorphous lithium phosphorus oxyntirde (Lipon) electrolytes on the surfaces of LiMn1.5Ni0.5O4 and LiCoO2 particles by a RFmagnetron sputtering technique [4,5]. Uniform subnanometer thick Lipon improved the cycling behaviors of LiMn1.5Ni0.5O4 cells dramatically, but did not impede the Mn dissolution. Although a thicker Lipon layers of a few nanometers were effective in preventing the Mn dissolution, the Lipon layers greatly reduced the specific capacity because Lipon has a very low electronic conductivity of ~10 -14 S/cm. For comparison, nanometerthick protective films of electronic/ionic mixed conductor are being evaluated. Half-cell performances of cathodes fabricated with LiMn1.5Ni0.5O4 particles coated with mixed conductor will be reported for cycling at room and