Improving the Electrochemical Performance of a Lithium-Rich Layered Cathode with an In Situ Transformed Layered@Spinel@Spinel Heterostructure
Shenghua Yuan,Jian Guo,Yue Ma,Ying Zhou,Hongzhou Zhang,Dawei Song,Xixi Shi,Lianqi Zhang
DOI: https://doi.org/10.1021/acsaem.1c01955
IF: 6.4
2021-10-11
ACS Applied Energy Materials
Abstract:Lithium-rich layered oxides have attracted much attention due to their high discharge capacity (>250 mA h·g–1). However, lithium-rich layered cathodes suffer from poor rate capabilities and voltage decay, which seriously limit their practical application. Herein, a unique @spinel double-spinel shell heterostructure is designed and successfully synthesized via coprecipitation and high-temperature solid-phase methods. In particular, lithium-rich layered oxides show good rate capabilities and high capacity retention when the molar amount of cobalt acetate and manganese acetate is 5%. After 100 cycles at 0.2 C, a discharge capacity of 232 mA h g–1 and a capacity retention of 92.7% can be obtained. The superior electrochemical performance of the in situ-transformed Li-rich layered cathode can be attributed to the unique three-dimensional diffusion channels for Li ions of the surface spinel phase. Besides, the in situ-transformed LiCoMnO4 shell can also improve the structural stability of the Li-rich layered oxides by reducing the side reactions and protecting the material from being corroded by the electrolyte. This study provides a strategy for surface modification, which can effectively improve the electrochemical performance of Li-rich layered cathode materials with high performance.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.1c01955.SEM image of the precursor Ni1/6Co1/6Mn4/6CO3 and the corresponding mapping spectrum; ex situ XRD spectra of the LLO and LSS-0.05 samples; EDS line scan of the selected area and the corresponding HTEM diagram of the LSS-0.05 sample; CV and dQ/dV curves of the first three cycles of the LLO, LSS-0.05, and LSS-0.1 samples; initial charge and discharge curves of LiCoMnO4, LSS-0.2, and LSS-0.4 samples; discharge curves of LLO, LSS-0.05, and LSS-0.1 samples at different rates and with different cycles; typical single titration curve of GITT measurements; equivalent circuit of half-cells; and EIS spectra of LLO, LSS-0.05, and LSS-0.1 samples in the initial cycle (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels