Novel two‐step method for joining alumina ceramic by using Al2O3 powder followed by glass infiltration
Mu Tang,Weiwei Zhu,Haohao Zou,Guoqing Zu,Ying Han,Xu Ran
DOI: https://doi.org/10.1111/jace.20298
IF: 4.186
2024-12-12
Journal of the American Ceramic Society
Abstract:A novel two‐step joining method was developed to join alumina ceramics for high‐temperature applications. Firstly, alumina ceramics were bonded using Al2O3 powder at 1550°C. Subsequently, the Dy2O3‐Al2O3‐SiO2 glass was infiltrated into the interlayer at 1450°C to obtain the alumina/alumina joints with dense composite interlayer composed by Al2O3, Dy2Si2O7, and few glass phase. The flexural strength of the joints at 1000°C reached about 90% of that of alumina ceramics under the same conditions. After the thermal cycles from room temperature to 1000°C for 50 times, there was no significant change in the flexural strength of the joints. In this work, a novel two‐step joining method was developed to join alumina ceramics for high‐temperature applications. First, alumina ceramics were bonded using Al2O3 powder at 1550°C. Subsequently, the Dy2O3–Al2O3–SiO2 glass was infiltrated into the interlayer at 1450°C to obtain the alumina/alumina joints with dense composite interlayer composed by Al2O3, Dy2Si2O7, and few glass phase. The content of Al2O3 in the composite interlayer reached 52.7%. As a result, the coefficient of thermal expansion mismatch between the interlayer and the alumina ceramic was reduced to only 2%. The flexural strength of the joints at room temperature was equivalent to that of the alumina ceramic. Furthermore, the flexural strength of the joints at 1000°C reached about 90% of that of alumina ceramics under the same conditions. After the thermal cycles from room temperature to 1000°C for 50 times, there was no significant change in the flexural strength of the joints.
materials science, ceramics