Abstract:To expand the application of SiC/SiC joints under extreme conditions, Nano-Infiltration and Transient Eutectic (NITE) joining technology with AlN-Y 2 O 3 as a sintering additive was successfully developed. The rheological properties of the slurry and the microstructure evolution of the joints were systematically characterized by rheometer, SEM, EDS, EBSD, and TEM, respectively. Both room-temperature and high-temperature flexural strength was measured to evaluate the mechanical properties of the joints. An immersion test with concentrated nitric acids was performed to evaluate the corrosion resistance of the joints. The defect-free joining layer was composed of a dense α-SiC phase, a small amount of YAG(Y 3 Al 5 O 12 ) distributed in the triangular grain boundary, and a Y-Al-O glass phase from AlN-Y 2 O 3 . The mechanism of NITE joining could be attributed to the incoherent growth of the newly generated α-SiC in the joining layer along the α-SiC substrate. The maximum room-temperature strength of the joints was 320.5 ± 37.6 MPa. When the test temperatures were 1000 °C, 1200 °C, and 1400 °C, the flexural strength reached 238.7 ± 33.1 MPa, 215.5 ± 52.5 MPa, and 166.9 ± 52.0 MPa, respectively. After immersing the joints in a concentrated HNO 3 for 168 h, the flexural strength was 173.3 ± 12.6 MPa. The joints' excellent mechanical properties and corrosion resistance reveal great application potential under extreme conditions.

Joining of Cf/SiC composites and Si<sub>3</sub>N<sub>4</sub> ceramic with Y<sub>2</sub>O<sub>3</sub>-Al<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub> glass filler for high-temperature applications

Microstructure and Properties of Porous Si3N4/Dense Si3N4 Joints Bonded Using RE–Si–Al–O–N (RE = Y or Yb) Glasses

Microstructure and Properties of Porous Si3N4/Dense Si3N4 Joints Bonded Using RE-Si-Al-O-N (RE = Y or Yb) Glasses

Microstructure, Mechanical Property and Bonding Mechanism of SiC Ceramic Joint Using a Novel Y2Si2O7/Mullite Glass-Ceramic Interlayer

Joining Dense Si3N4 to Porous Si3N4 Using a Novel Glass-Ceramic Interlayer with Precipitated Β-Lialsi2o6/mg2sio4

Joining of SiC ceramics using CaO-Al<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub> (CAS) glass ceramics

Near-seamless joining of Cf/SiC composites using Y3Si2C2 via electric field-assisted sintering technique

Joining of SiC ceramics using CaO-Al2O3-SiO2 (CAS) glass ceramics

Microstructure Evolution and Mechanical Properties of Porous Si3N4 and Dense Si3N4 Joints Bonded Using CaO–Li2O-Al2O3–SiO2 Glass-Ceramic

Joining of Si3N4 Ceramics with In-situ Formed Oxynitride Glass Interlayer

Joining Pre-Oxidized Dense Si3N4 to Porous Si3N4 with Β-Spodumene Based Glass-Ceramic Interlayer

Pressure-less joining of SiCf/SiC composites by Y2O3–Al2O3–SiO2 glass: Microstructure and properties

Joining of SiC ceramics by combining NITE-SiC interlayer and its thickness control

Microstructure and mechanical properties of SiC joint using anorthite based glass-ceramic and first principles calculation of joint interface

Heat-resistant Joints of Si3N4 Ceramics with Intermetallic Compounds Formed in Situ

Nano-infiltration and transient eutectic (NITE) joining of SiC ceramics applied for the harsh environments

Microstructure and Strength of Si3N4 Joints Bonded with Sialon-Oxynitride Glass

Effect of SiC Nanowires on the Thermal Shock Resistance of Joint Between Carbon/carbon Composites and Li2O–Al2O3–SiO2 Glass Ceramics

Microstructure and Formation Mechanism of Cf/SiC and Nb Joint Brazed with Laminated Amorphous Ti–Zr–Cu–Ni/crystalline Ti Composite Filler

Joining Silicon Nitride Ceramics In Air By Pure Aluminum Filler

Evaluation of Low-Temperature Glass Fillers and Joining of Reaction-Bonded Silicon Carbide Ceramics at Vacuum