Abstract:Prepared with pure Ti and Si powders as raw materials, the Ti16Si84 alloy (at. %) was obtained through refining in an intermediate frequency magnetic induction furnace. In this study, a novel method to join SiC fiber-reinforced SiC matrix composites (SiCf/SiC composites) under non-pressurized conditions is proposed using Ti16Si84 alloy foil as the joining material. The joining process was optimized, and the wettability, microscopic morphology, and bonding reaction of the joint were studied, along with the fracture characteristics and the bonding mechanism. Additionally, the corrosion resistance of the joints was examined in pure static water with high-dissolved oxygen (246 ppm) at 360 °C and 18.6 MPa. The results showed that Ti16Si84 alloy has good wettability with SiCf/SiC, enabling it to join SiCf/SiC successfully. The joint was composed of SiC, TiSi2, and Si, and there was no intermediate between them. When the brazing temperature was 1410 °C, the shear strength of the joint reached 42.5 MPa, and the joint integrity was favorable. After the shear test, numerous SiCf/SiC composites were torn by the solder, indicating their advantageous shear properties and high joint strength. After three days of corrosion, the joint samples' weight showed almost no changes. The corrosion depth was less than 20 μm and the residual shear strength of the corroded joined samples was 38.37 MPa, indicating excellent hydrothermal corrosion resistance of the joint material.

Joining of Cf/SiC composites using AlCoCrFeNi2.1 eutectic high‐entropy alloy filler by spark plasma sintering

Microstructure and Mechanical Properties of Cf/SiC Composite Joints Joined Using AlCoCrFeNi2.1 Eutectic High-Entropy Alloy Filler Via Spark Plasma Sintering

Microstructure and mechanical properties of C f /SiC composite joints joined using AlCoCrFeNi 2.1 eutectic high-entropy alloy filler via spark plasma sintering

Reaction Mechanisms and Mechanical Properties of SiCf/SiC Composite and GH536 Superalloy Joints Using CoFeNiCrMn High-Entropy Alloy Filler

Joining SiCf/SiC Composites to Al0.3CoCrFeNi High-Entropy Alloys with a Cu–Ti Filler Alloy: Interfacial Reactions, High-Entropy Effects, and Mechanical Properties

Joining C/C composite in a few seconds using refectory high entropy alloy fillers via spark plasma sintering

Brazing SiC Ceramic to Al0.3CoCrFeNi High‐entropy Alloy Using Ag–Cu Filler Metal

Microstructural evolution and mechanical property of a SiCf/SiC composite/Ni-based superalloy joint brazed with an Au-Cu-Ti filler

Joining of C/C composite with high entropy alloy interlayers via spark plasma sintering and its mechanical strength at 1600 °C

SiC fiber strengthened Si-14Ti high-temperature filler alloy for brazing SiCf/SiC and C/C composites

A Study of the SiCf/SiC Composite/ni-Based Superalloy Dissimilar Joint Brazed with a Composite Filler

Microstructure and mechanical properties of SiCf/SiC composites/ GH536 superalloy joints brazed with CoFeNiCrCu high-entropy alloy filler

Achieving SiC Joints with Outstanding High-Temperature Property Via Flash Brazing Using FeCoCrNiCu High-Entropy Alloy

SiC fiber strengthened Si 14Ti high-temperature filler alloy for brazing SiC f /SiC and C/C composites

Microstructure and properties of pressure-less joining of SiCf/SiC composites by Ti–Si alloys

Ultrafast low-temperature near-seamless joining of Cf/SiC using a sacrificial Pr3Si2C2 filler via electric current field-assisted sintering technique

Joining of SiC using CoFeCrNiCuTi high entropy alloy filler by electric current field assisted sintering

Near-seamless joining of Cf/SiC composites using Y3Si2C2 via electric field-assisted sintering technique

Effects of Joining Conditions on Microstructure and Mechanical Properties of C F /al Composites and TiAl Alloy Combustion Synthesis Joints

Brazing SiC Ceramics and Zr with CoCrFeNiCuSn High Entropy Alloy

Microstructure Evolution and Mechanical Properties of SiC/Mo Joint Brazed with FeCoCrNi High-Entropy Alloy Filler