Abstract:Hot pressing was used to produce compact ceramic samples with the following composition (wt.%): 60 ZrB2 + 20 SiC + 20 (Al2O3 + 32 t-ZrO2). The tetragonal modification of zirconium oxide in the eutectic was stabilized by yttrium oxide. The porosity of the samples was 3–5%. The mechanical properties of the ceramics (hardness HV, fracture toughness KIc, tensile strength δf, compressive strength Y, grain-boundary strength S, and bending strength σ) were studied. Analysis of the microstructure and elemental composition of the phases revealed that a defect-free structure developed in the ZrB2-based composite through strong Van Der Waals adhesive interaction at the SiC–Al2O3 interface, which increased the fracture toughness to 9.4 MPa ∙ m1/2. In turn, this increased the grain strength from 0.64 GPa for the basic composite to 3.46 GPa for the ZrB2–SiC composite with an oxide addition. An addition of Al2O3 + 32 wt.% t-ZrO2 was introduced in sufficient quantities not only to reduce the fracture stress but also to promote plastic deformation of the material for high-temperature bending strength. Study of the oxidation process showed that the weight increment of the 60 wt.% ZrB2 + 20 wt.% SiC + 20 wt.% (Al2O3 + 32 wt.% t-ZrO2) sample at 1600°C for a holding time of 1 h was stabilized by dense oxide scale formed on the material, while the weight increment of the ZrB2 + 20 wt.% SiC sample and, consequently, the scale thickness increased monotonically. The scale that formed on the ZrB2 + 20 wt.% SiC samples with an addition of Al2O3 + 32 wt.% t-ZrO2 consisted of an upper Al2SiO5-based layer 50 μm thick with ZrO2 inclusions and a lower ZrO2-based layer up to 80 μm thick with Al2SiO5 inclusions. The eutectic Al2O3 + 32 wt.% t-ZrO2 oxide addition to the basic ZrB2–SiC system had higher oxidation resistance and thus prevented the diffusion of oxygen into the material.

Thermal Shock Behavior of ZrB2–SiC Composite Ceramics with Added TaSi2

Thermal shock behavior of ZrB2–SiC ultra-high temperature ceramics with addition of zirconia

The Influence of Surface Heat Transfer Conditions on Thermal Shock Behavior of ZrB2–SiC–AlN Ceramic Composites

High temperature oxidation behavior and mechanism of SiC-TaB2 composites

Microstructure, Mechanical Properties and Thermal Shock Resistance of Zirconium Diboride Containing Silicon Carbide Ceramic Toughened by Carbon Black

Mechanical and Corrosion Properties of ZrB2–SiC Composite Ceramics with Oxide Additions

Microstructure and Thermal Shock Resistance of Zr7/8Ti1/8B2-20 Vol% SiC Composites Synthesized by Mechanical Alloying and Spark Plasma Sintering

Microstructure and thermal shock behavior of ZrB2–SiC–graphite composite

The repeated thermal shock behaviors of a ZrB2–SiC composite heated by electric resistance method

Microstructural Evolution and Performance of Carbon Fiber-Toughened ZrB2 Ceramics with SiC or ZrSi2 Additive

Thermal Shock Behavior of Porous ZrB2–SiC Ceramics

Enhanced Mechanical Properties, Thermal Shock Resistance and Oxidation Resistance of Si2BC3N Ceramics with Zr-Al Addition

Microstructural feature and thermal shock behavior of hot-pressed ZrB2–SiC–ZrO2 composite

Effect of SiC Content on Mechanical Properties and Thermal Shock Resistance of BN–ZrO2–SiC Composites

High‐Temperature Oxidation at 1900°C of ZrB2–xSiC Ultrahigh‐Temperature Ceramic Composites

Repeated Thermal Shock Behavior of the ZrB2–SiC–ZrC Ultrahigh-Temperature Ceramic

β→α Phase Transformation and Properties of Solid-State-Sintered SiC Ceramics with TaC Addition

Enhanced Mechanical Properties, Thermal Shock Resistance and Ablation Resistance of Si2BC3N Ceramics with Nano ZrB2 Addition

Microstructure and mechanical properties of SiC composite ceramics modified by (TixZr1–x)B2 solid solution

Enhanced Strengths and Thermal Shock Resistance of SiC-BN-10 Vol% Cf Composites Through ZrB2 Addition

Microstructure Characterization of ZrB2–SiC Composite Fabricated by Spark Plasma Sintering with TaSi2 Additive