Synthesis of High Surface Area Nanometer Magnesia by Solid-State Chemical Reaction
Guan Hongbo,Wang Pei,Zhao Biying,Zhu Yuexiang,Xie Youchang
DOI: https://doi.org/10.1007/s11458-007-0041-5
2007-01-01
Frontiers of Chemistry in China
Abstract:Nanometer MgO samples with high surface area, small crystal size and mesoporous texture were synthesized by thermal decomposition of MgC2O4 · 2H2O prepared from solid-state chemical reaction between H2C2O4 · 2H2O and Mg (CH3COO)2 · 4H2O. Steam produced during the decomposition process accelerated the sintering of MgO, and MgO with surface area as high as 412 m2 · g−1 was obtained through calcining its precursor in flowing dry nitrogen at 520°C for 4 h. The samples were characterized by X-ray diffraction, N2 adsorption, transmission electron microscopy, thermogravimetry, and differential thermal analysis. The as-prepared MgO was composed of nanocrystals with a size of about 4–5 nm and formed a wormhole-like porous structure. The MgO also had good thermal stability, and its surface areas remained at 357 and 153 m2·g−1 after calcination at 600 and 800°C for 2 h, respectively. Compared with the MgO sample prepared by the precipitation method, MgO prepared by solid-state chemical reaction has uniform pore size distribution, surface area, and crystal size. The solid-state chemical method has the advantages of low cost, low pollution, and high yield, therefore it appears to be a promising method in the industrial manufacture of nanometer MgO.