Abstract:Magnesia nanopowder with different particle sizes (10-100 nm) and different crystallinity was synthesized by the sol -gel method from an Mg(NO3 )2·6H2O precursor. The mechanism of gel formation in the presence of citric acid, the factors that affect the stability of sol - gel, including the amount of water, ethanol and complexing reagent, and the influences of calcining temperature on the particle size and crystallinity of MgO particles were investigated. The results indicate that when citric acid is not introduced into the system, the stability of gel is poor and therefore the MgO powders obtained have a large particle size and there is serious agglomeration. Citric acid can effectively enhance the stability of gel and a stable gel is formed when the mole ratio of water, magnesium nitrate, citric acid and ethanol is 100 : 9 : 9 : 2. 1. The calcining temperature has no remarkable effect on the chemical composition and crystal shape of prepared MgO powders. However, the calcining temperature has a significant effect on the particle size and the crystallinity of MgO. When the calcining temperature is 500℃, low crystalline magnesia powder with a particle size of about 10 nm and certain agglomeration is produced, while calcining at 600℃ forms MgO powder with a particle size of 30-60 nm and with good crystallinity and uniform dispersion. MgO powder with a particle size of 50-100 nm with better crystallinity and a perfect crystal structure is obtained at 900℃.

Simple Synthesis of Single-crystalline Nanoplates of Magnesium Oxide

A simple solution calcination route to porous MgO nanoplates

Synthesis And Characterization Of Porous Magnesium Hydroxide And Oxide Nanoplates

Facile synthesis of magnesium oxide nanoplates via chemical precipitation

Facile and rapid synthesis of nanoplates Mg(OH)2 and MgO via Microwave technique from metal source: structural, optical and dielectric properties

Large-scale synthesis of single-crystalline MgO with bone-like nanostructures

Synthesis of MgO Microspheres with Nanosheets in a Mechanical Force Reactor and Its Optical Property

Nanoscale magnesium hydroxide and magnesium oxide powders: Control over size, shape, and structure via hydrothermal synthesis

SYNTHESIS OF NANOMETER MAGNESIA BY SOL- GEL METHOD

Synthesis, Characterization and Optical Properties of Mg(OH)2 Micro-/Nanostructure and Its Conversion to MgO

Synthesis of High Surface Area Nanometer Magnesia by Solid-State Chemical Reaction

γ-Bi2MoO6 nanoplates: Surfactant-assisted hydrothermal synthesis and optical properties

Fabrication of Tubular Magnesium Oxide Nanocrystals Via Combining Ammonium Sulfate Leaching and Precipitation Method and It's Crystal Growth Behavior

Preparation of Magnesia Nanoballs from Dolomite

(NaPO3)6-assisted wet formation of dispersive Mg(OH)2 nanoplates

Synthesis of Mg(Oh)(2) Nanoparticles from Mgo Using Magnesium Acetate As Additive

Preparation of Nanometer Oxide Magnesium

Synthesis and Characterization of MgO Single-Crystalline One-Dimensional Nanostructures

Electrosynthesis and catalytic properties of magnesium oxide nanocrystals with porous structures

Synthesis, Characterization of Monodispersed MgO Microspheres and Thermal Decomposition Kinetics of Its Precusor

Synthesis of Nano Magnesium Oxide from Dolomite via Ammonium Sulfate Leaching