Abstract:High-purity magnesia refractories were fabricated by brine magnesium hydroxide from the salt-lake brine (Qinghai Salt Lake) and Y2O3 as an additive at 1780(degrees)C. It avoided the substantial CO2 emissions and ultra high temperature sintering process (>1900(degrees)C) when compared with the conventional magnesite-calcination technical approach. The results confirmed that Y2O3 was dispersed on the MgO grains boundaries in the fabricated MgO aggregates, resulting in a decrease in apparent porosity and enhancing the grains' boundaries. With 3 wt% addition of Y2O3, the apparent porosity and bulk density of the sample reached to 15.9 % and 3.10 g/cm(3 )from 37.9 % to 2.30 g/cm(3 ) of blank control group, respectively. Compared to the blank control without Y2O3-adding, 2 O 3-adding, the sample with 5 wt% Y2O3 exhibited a 54.17 % increase in the resistance to molten slag. SEM results indicated that the incorporation of Y2O3 in samples increased the porosity of small pores and enhanced grains boundaries, thereby suppressing slag's penetration. Furthermore, the Y2O3-adding -adding was employed to disperse the MgO grains boundaries and existed as separate phases for grains boundaries enhancement. The slag attack of the fabricated MgO-Y(2)O(3 )refractory raw materials were controlled by an inter-crystalline corrosion process.

Synthesis of MgO Microspheres with Nanosheets in a Mechanical Force Reactor and Its Optical Property

Study on Preparation of MgO Crystal Whisker from Magnesite

Microstructue and Optical Properties of Mg-doped ZnO Thin Films Prepared by Sol-gel Method

Fabrication of Y2O3-doped MgO Refractory Raw Materials Based on Magnesium Hydroxide from Salt-Lake Brine

Preparation and Characterization of Mg-doped ZnO Thin Films by Sol–gel Method

Simple Synthesis of Single-crystalline Nanoplates of Magnesium Oxide

Synthesis, structural and luminescence properties of MgO, Mg 2 SiO 4 and MgO/Mg 2 SiO 4 nanostructures

MgO nanostructures synthesized by thermal evaporation

Synthesis and Characterization of MgO Single-Crystalline One-Dimensional Nanostructures

Large-scale synthesis of single-crystalline MgO with bone-like nanostructures

Synthesis of High Surface Area Nanometer Magnesia by Solid-State Chemical Reaction

Nanoflake-Modified Mgo Microspheres Prepared by Flame Spraying

Self-assembled Growth of MgO Nanosheet Arrays Via a Micro-Arc Oxidation Technique

Magnesium catalyzed growth of SiO2 hierarchical nanostructures by a thermal evaporation process

Kinetics-driven growth of orthogonally branched single-crystalline magnesium oxide nanostructures.

Synthesis of Nanostructured MgO Powders with Photoluminescence by Plasma-Intensified Pyrohydrolysis Process of Bischofite from Brine

Synthesis of Magnesium Borate Nanorods by Sol-Gel Process

Direct Observation of the Growth Process of MgO Nanoflowers by a Simple Chemical Route.

Synthesis of MgO nanotube bundles

Local super-saturation dependent synthesis of MgO nanosheets

Formation of non-cubic nanoparticles from cubic MgO in intensified self-burning of magnesium