Abstract:Nanometer MgO samples with high surface area, small crystal size and mesoporous texture were synthesized by thermal decomposition of MgC2O4 · 2H2O prepared from solid-state chemical reaction between H2C2O4 · 2H2O and Mg (CH3COO)2 · 4H2O. Steam produced during the decomposition process accelerated the sintering of MgO, and MgO with surface area as high as 412 m2 · g−1 was obtained through calcining its precursor in flowing dry nitrogen at 520°C for 4 h. The samples were characterized by X-ray diffraction, N2 adsorption, transmission electron microscopy, thermogravimetry, and differential thermal analysis. The as-prepared MgO was composed of nanocrystals with a size of about 4–5 nm and formed a wormhole-like porous structure. The MgO also had good thermal stability, and its surface areas remained at 357 and 153 m2·g−1 after calcination at 600 and 800°C for 2 h, respectively. Compared with the MgO sample prepared by the precipitation method, MgO prepared by solid-state chemical reaction has uniform pore size distribution, surface area, and crystal size. The solid-state chemical method has the advantages of low cost, low pollution, and high yield, therefore it appears to be a promising method in the industrial manufacture of nanometer MgO.

Local super-saturation dependent synthesis of MgO nanosheets

Synthesis and Characterization of MgO Single-Crystalline One-Dimensional Nanostructures

Synthesis of MgO nanotube bundles

Synthesis and Orientational Assemblies of MgO Nanosheets with Exposed (111) Facets

MgO nanostructures synthesized by thermal evaporation

Synthesis and Characterization of Dendritic ZnMgO Nanostructures

Synthesis of Magnesium Borate Nanorods by Sol-Gel Process

Large-scale synthesis of single-crystalline MgO with bone-like nanostructures

Kinetics-driven growth of orthogonally branched single-crystalline magnesium oxide nanostructures.

Synthesis of MgO Microspheres with Nanosheets in a Mechanical Force Reactor and Its Optical Property

Simple Synthesis of Single-crystalline Nanoplates of Magnesium Oxide

Synthesis of MgO Nanowires Combined with C Nanotubes

Preparation and characterization of lamellar-like Mg(OH)2 nanostructures via natural oxidation of Mg metal in formamide/water mixture

Self-assembled Growth of MgO Nanosheet Arrays Via a Micro-Arc Oxidation Technique

Synthesis of High Surface Area Nanometer Magnesia by Solid-State Chemical Reaction

Magnesium catalyzed growth of SiO2 hierarchical nanostructures by a thermal evaporation process

ZnMgO Nanorod Arrays Grown by Metal-Organic Chemical Vapor Deposition

Synthesis And Characterization Of New-Type Mgo Nanobelts Via Co-Precipitation Synthetic Way

Preparation of MgO Nanosheets with Polar (111) Surfaces by Ligand Exchange and Esterification – Synthesis, Structure, and Application As Catalyst Support

Direct Observation of the Growth Process of MgO Nanoflowers by a Simple Chemical Route.

Single Crystalline Znmgo Pleated Nanosheets and Quasinanotubes