Abstract:Nanometer MgO samples with high surface area, small crystal size and mesoporous texture were synthesized by thermal decomposition of MgC2O4 · 2H2O prepared from solid-state chemical reaction between H2C2O4 · 2H2O and Mg (CH3COO)2 · 4H2O. Steam produced during the decomposition process accelerated the sintering of MgO, and MgO with surface area as high as 412 m2 · g−1 was obtained through calcining its precursor in flowing dry nitrogen at 520°C for 4 h. The samples were characterized by X-ray diffraction, N2 adsorption, transmission electron microscopy, thermogravimetry, and differential thermal analysis. The as-prepared MgO was composed of nanocrystals with a size of about 4–5 nm and formed a wormhole-like porous structure. The MgO also had good thermal stability, and its surface areas remained at 357 and 153 m2·g−1 after calcination at 600 and 800°C for 2 h, respectively. Compared with the MgO sample prepared by the precipitation method, MgO prepared by solid-state chemical reaction has uniform pore size distribution, surface area, and crystal size. The solid-state chemical method has the advantages of low cost, low pollution, and high yield, therefore it appears to be a promising method in the industrial manufacture of nanometer MgO.

Synthesis And Characterization Of New-Type Mgo Nanobelts Via Co-Precipitation Synthetic Way

Synthesis and Characterization of Single Crystalline Mnooh and Mno2 Nanorods by Means of the Hydrothermal Process Assisted with Ctab

MgO nanostructures synthesized by thermal evaporation

Synthesis and Characterization of MgO Single-Crystalline One-Dimensional Nanostructures

Synthesis of MgO Nanowires Combined with C Nanotubes

Synthesis of Magnesium Borate Nanorods by Sol-Gel Process

Preparation and Characterization of Porous Mgo and Nio/Mgo Nanocomposites

Synthesis of MgO nanotube bundles

Synthesis of Mg(Oh)(2) Nanoparticles from Mgo Using Magnesium Acetate As Additive

Fabrication of Mgo Hierarchical Nanostructures by A Thermal Evaporation Method

MgCO 3·3H 2O and MgO complex nanostructures: Controllable biomimetic fabrication and physical chemical properties

Preparation and characterization of lamellar-like Mg(OH)2 nanostructures via natural oxidation of Mg metal in formamide/water mixture

Synthesis of Zn 1− x Mg x O alloyed nanostructures and the crystal evolution in annealing process

Synthesis And Characterization Of Porous Magnesium Hydroxide And Oxide Nanoplates

Nanosized MgO Powder Preparation by Homogeneous Precipitation-Post Annealing Method Using Mg(NO3)2·6H2O as Raw Material

Synthesis and Characterization of Dendritic ZnMgO Nanostructures

Nanoscale magnesium hydroxide and magnesium oxide powders: Control over size, shape, and structure via hydrothermal synthesis

Synthesis of High Surface Area Nanometer Magnesia by Solid-State Chemical Reaction

Formation of rod-like Mg(OH)2 nanocrystallites under hydrothermal conditions and the conversion to MgO nanorods by thermal dehydration

Local super-saturation dependent synthesis of MgO nanosheets

Solvothermal Synthesis of Mg(OH)2nanotubes Using Mg10(OH)18Cl2·5H2O Nanowires As Precursors