Abstract:Parameter effects on the preparation for nanosized particles of magnesium hydroxide from dolomite via carbonation were investigated. The effects of precipitator and reaction temperature on the morphology of the nanosized particles were evaluated. The improvement of surface active agent on the dispersion of the particles was analyzed. The reaction mechanism of the experiment was discussed. The results show that the crystallization of magnesium hydroxide using ammonia as a precipitator is better than that using sodium hydroxide as a precipitator, and the nanosized particles of magnesium hydroxide appear an approximately thin sheet of hexagons with an average particle size of 16 nm. The smaller crystal nuclei of magnesium hydroxide with the thickness of about 5–7 nm and the size of 10–15 nm could be prepared at the reaction temperature of 30 ℃. The crystal nuclei started to grow larger with the disordered arrangement at 50 ℃. The integrated crystalline grains of magnesium hydroxide with the thickness of about 10 nm and the size of 10–20 nm could be prepared at 70 ℃. However, the irregular arrangement could occur at 80 ℃ . In addition, the dispersion of the nanosized crystalline grains of magnesium hydroxide could be improved by using polyethylene glycol (PEG) or sodium dodecyl sulfate (SDS) as surface active agents. Then the thickness of the nanosized particles is 10 nm. The dispersion performance became superior at an optimized amount of PEG of 3.0%. The dispersion was more efficient at the amount of SDS of 4.0% and its size is 20 nm.

Nanosized MgO Powder Preparation by Homogeneous Precipitation-Post Annealing Method Using Mg(NO3)2·6H2O as Raw Material

Preparation of Nanometer Magnesia with High Surface Area and Study on the Influencing Factors of the Preparation Process

PREPARATION OF NiO NANOPARTICLES ON THE SILICA SURFACE BY ADSORPTION PHASE SYNTHESIS AND ITS REGULATION ON MORPHOLOGY OF NiO PARTICLES

Nanoscale magnesium hydroxide and magnesium oxide powders: Control over size, shape, and structure via hydrothermal synthesis

Preparation and Application of Nano - Mg2B2O5

MgO nanostructures synthesized by thermal evaporation

Synthesis of MgO powders by precipitant for transparent ceramics

PREPARATION OF NANOSIZED Bi3.25 La0.75 Ti3 O12 POWDER BY COPRECIPITATION METHOD

Synthesis of High Surface Area Nanometer Magnesia by Solid-State Chemical Reaction

PARAMETER EFFECTS ON PREPARATION OF NANOSIZED PARTICLES OF MAGNESIUM HYDROXIDE FROM DOLOMITE AND THEIR CHARACTERS

Preparation of Magnesium Hydroxide Chloride Hydrate Nanowires Using Calcined Dolomite

A simple direct preparation of nanocrystalline γ-Mn2O3 at ambient temperature

Preparation of Ccalcining MgO and its precursor

Preparation of highly-dispersed Mg(OH)2 powders and influence factors

Preparation of nano-sized lanthanum oxide by ultrasonic-homogeneous precipitation method

Preparation of MoO 3 powder by hydrothermal method

Synthesis and performances of nano-sized neodymium oxide

A study on preparation of ultrafine powders of Ni(OH)2 and NiO with different shapes by precipitation transformation method

Synthesis And Characterization Of New-Type Mgo Nanobelts Via Co-Precipitation Synthetic Way

Preparation and Characterization of Porous Mgo and Nio/Mgo Nanocomposites

Preparation And Characterization Of Nano-Crystalline Mgnb2o6 Microwave Dielectric Powder