Abstract:Abstract Based on the raw material of ammonium tetramolybdate in the experiment, molybdenum trioxide was prepared by hydrothermal synthesis, and the effects of different pH, hydrothermal reaction time, filling degree, and calcination temperature on molybdenum trioxide powder were studied. Meanwhile, the molybdenum trioxide powder was characterized through scanning electron microscopy, transmission electron microscopy, X-ray diffraction, and thermal analysis differential scanning calorimetry analysis so as to study the morphology and phase changes during the experiment. As is evident from the research findings, MoO 3 powders with uniform and suitable size, smooth and clear surface, good dispersibility, and no adhesion can be obtained at the conditions of pH = 1, 16 h hydrothermal reaction, 90% of filling degree, and 550°C of calcination temperature. In the calcination process, MoO 3 crystal undergone crystal transformation and was completely transformed from h-MoO 3 to α-MoO 3 at the calcination temperature of 350°C.

What problem does this paper attempt to address?

The problem this paper attempts to address is how to efficiently prepare molybdenum trioxide (MoO₃) powder with uniform particle size, good dispersibility, and no agglomeration through the hydrothermal method. Specifically, the researchers explored the effects of different pH values, hydrothermal reaction times, filling degrees, and calcination temperatures on the morphology and phase transformation of MoO₃ powder, aiming to find the optimal preparation conditions. The study found that under the conditions of pH=1, 16 hours of hydrothermal reaction time, 90% filling degree, and 550°C calcination temperature, MoO₃ powder with uniform particle size, smooth surface, good dispersibility, and no agglomeration can be obtained. Additionally, the research discovered that at a calcination temperature of 350°C, MoO₃ crystals completely transform from the hexagonal phase to a stable orthorhombic phase. This research is of great significance for the preparation of nano-scale, high-purity MoO₃ powder and high-performance molybdenum alloys, as the MoO₃ powder particles prepared by traditional processes are rough and uneven in size, failing to meet the requirements of these applications. By optimizing the hydrothermal preparation process, the quality of MoO₃ powder can be significantly improved, thus providing a better raw material foundation for the subsequent preparation of molybdenum powder and molybdenum alloys.

Preparation of MoO 3 powder by hydrothermal method