Abstract:In this experiment, we investigated the effects of different reactions on the growth process and morphology of h-MoO3 and α-MoO3, and their optical properties and photocatalytic activities were also investigated. Orthogonal experiments were designed to investigate the effects of four influencing factors, namely the amount of ammonium molybdate tetrahydrate (AHM), the type of acid, the reaction temperature and the holding time, on the morphology of h-MoO3 by a microwave hydrothermal method. The phase and morphology were analyzed by using advanced physicochemical techniques. The XRD results showed that the samples produced by the microwave hydrothermal method had sharp diffraction peaks, high crystallinity and complete crystalline shape. AHM generates h-MoO3 in both hydrochloric and nitric acid environments. In particular, when the temperature rises to 200 °C, the generated h-MoO3 will be converted to α-MoO3 in a nitric acid environment, which will be generated in a sulfuric acid environment. Therefore, increasing the reaction temperature will result in the conversion of h-MoO3 to α-MoO3 in sulfuric acid solution. SEM results show that the sample prepared from hydrochloric acid solution has a complete hexagonal prism morphology, while the sample prepared from sulfuric acid solution presents a long fibrous morphology, and the sample prepared from nitric acid solution has many defects on the surface of the hexagonal prism morphology. Interestingly, sample A11 prepared in nitric acid solution showed a spherical structure. Since the generated A3, A6 and A9 samples are all stable phase α-MoO3, they have a wider band gap compared with other samples. Their particle size is up to the nanometer scale, so they have strong adsorption properties. The spherical sample A11 has excellent adsorption and photocatalytic activity.

Crystal Phase- and Morphology-Controlled Synthesis of MoO3materials

Hydrothermal Synthesis of MoO3 Nanobelts and Their Electrochemical Characterization

Single-crystalline Orthorhombic Molybdenum Oxide Nanobelts: Synthesis and Photocatalytic Properties

Thermal stability and photoluminescence property of hexagonal MoO3·0.55H2O microrods

Morphology-Controlled Synthesis of Pbmoo4 Crystals by A Simple Sonochemical Method

Aqueous and mechanical exfoliation, unique properties, and theoretical understanding of MoO3 nanosheets made from free-standing α-MoO3 crystals: Raman mode softening and absorption edge blue shift

The Growth Process and Photocatalytic Properties of h-MoO3 and α-MoO3 under Different Conditions

Synthesis and Characterization of Single Crystalline Mnooh and Mno2 Nanorods by Means of the Hydrothermal Process Assisted with Ctab

Preparation of MoO3nanostructures and Their Optical Properties

General Synthesis and Phase Control of Metal Molybdate Hydrates MMoO4·nH2O (M = Co, Ni, Mn, N = 0, 3/4, 1) Nano/Microcrystals by a Hydrothermal Approach: Magnetic, Photocatalytic, and Electrochemical Properties

Low-Temperature Synthesis of Large-Scale Single-Crystal Molybdenum Trioxide (moo3) Nanobelts

Charge Separation and Strong Adsorption-Enhanced MoO3 Visible Light Photocatalytic Performance

Hydrothermal Route to Single Crystalline Α-Moo3 Nanobelts and Hierarchical Structures

Controllable synthesis of Bi2MoO6 and effect of morphology and variation in local structure on photocatalytic activities

Molybdenum Trioxide Nanostructures Prepared by Thermal Oxidization of Molybdenum

Electrochromic Performance and Capacitor Performance of α-MoO3 Nanorods Fabricated by a One-Step Procedure

Controllable Hydrothermal Synthesis and Photocatalytic Performance of Bi2MoO6 Nano/Microstructures

Modified monoclinic metastable β-MoO 3 submicrospheres: controllable preparation, phase identification, and their formation mechanisms

Chemically Homogenizing MoO 2 Nanocrystals into Monodispersed Spherical Shapes for Enhanced Cr(VI) Photoreduction

Formation and Conversion Mechanisms Between Single-Crystal Gamma-Mnooh and Manganese Oxides

Facile Water-Based Strategy for Synthesizing MoO3–x Nanosheets: Efficient Visible Light Photocatalysts for Dye Degradation