Abstract:La0. 8Ca0. 2MnO3 nanowires were prepared by using a simple sol-gel method with nano-channel alumina(NCA) as template. The effects of two kinds of annealing methods. on the structure, morphology of La0. 8Ca0. 2MnO3 nanowires were investigated. The diameter of La0. 8Ca0. 2MnO3 nanowires prepared by ramping the furnace temperature directly to 800 degreesC with a rate of 10 degreesC/min is larger than that of pores within NCA. While, the diameter of La0. 8Ca0. 2MnO3 nanowires prepared by ramping the furnace temperature to 400 degreesC with a rate of 2 degreesC /min and keeping at this temperature for I h, then ramping to 800 degreesC with a rate of 10 degreesC /min and keeping at this temperature for 2 h is nearly equivalent to that of pores within NCA. XRD and selected area electron diffraction indicate that the nanowires derived under the two annealing conditions are of monoclinic perovskite structure. It is demonstrated that the La0. 8Ca0. 2MnO3 nanowires with monoclinic perovskite structure can be fabricated at low temperatures by employing a solution route. The method presented in this paper is also feasible for fabricating the nanowires of other mono-component and multi-component oxides.

A simple direct preparation of nanocrystalline γ-Mn2O3 at ambient temperature

Synthesis and Characterization of Single Crystalline Mnooh and Mno2 Nanorods by Means of the Hydrothermal Process Assisted with Ctab

A Facile Template-Free Preparation of Porous Manganese Oxides by Thermal Decomposition Method

Low Temperature Synthesis of Nanocrystalline Mn3o4 by A Solvothermal Method

Morphology-controlled Synthesis and Characterization of MnWO4 Nanocrystals Via a Facile, Additive-Free Hydrothermal Process

Preparation of MnO_2 Nanorod and Its Catalytic Performance

Hydrothermal Preparation and Characterization of MnWO4Nanowires

ChemInform Abstract: Shape‐Controlled Synthesis of MnWO4 Nanocrystals Via a Simple Hydrothermal Method.

Room Temperature Preparation of Nanocrystalline MnCuZn Ferrite Powder by Auto-Combustion of Nitrate-Citrate Gels

Synthesis of Nanocrystalline Cryptomelane from Reduction-Ammonia Leaching Residue of Ocean Manganese Nodules

Nanorods of Manganese Oxides: Synthesis, Characterization and Catalytic Application

Preparation of Mn3O4 Nanowires by Calcining the Precursor Powders Synthesized in a Novel Inverse Microemulsion

Facile and large-scale synthesis of single-crystalline manganese oxyhydroxide/oxide nanostructures

Shape‐ and Size‐Controlled Synthesis of Mn3O4 Nanocrystals at Room Temperature

Synthesis of Nanosized MnOOH Via Solvothermal Route

Preparation of Ultrafine MnO2 Powders by the Solid State Method Reaction of KMnO4 with Mn(II) Salts at Room Temperature

Nanosized MgO Powder Preparation by Homogeneous Precipitation-Post Annealing Method Using Mg(NO3)2·6H2O as Raw Material

Formation and Conversion Mechanisms Between Single-Crystal Gamma-Mnooh and Manganese Oxides

Fabrication and characterization of Lal(1.8)Ca(0.2)MnO(3) nanowires

Synthesis and characterization of reduced transition metal oxides and nanophase metals with hydrazine in aqueous solution

Controllable Synthesis and Characterization of Α-Mno 2 Nanowires