Nanorods of Manganese Oxides: Synthesis, Characterization and Catalytic Application

ZH Yang,YC Zhang,WX Zhang,X Wang,YT Qian,XG Wen,SH Yang

DOI: https://doi.org/10.1016/j.jssc.2005.11.028

IF: 3.3

2006-01-01

Journal of Solid State Chemistry

Abstract:Single-crystalline nanorods of β-MnO2, α-Mn2O3 and Mn3O4 were successfully synthesized via the heat-treatment of γ-MnOOH nanorods, which were prepared through a hydrothermal method in advance. The calcination process of γ-MnOOH nanorods was studied with the help of Thermogravimetric analysis and X-ray powder diffraction. When the calcinations were conducted in air from 250 to 1050°C, the precursor γ-MnOOH was first changed to β-MnO2, then to α-Mn2O3 and finally to Mn3O4. When calcined in N2 atmosphere, γ-MnOOH was directly converted into Mn3O4 at as low as 500°C. Transmission electron microscopy (TEM) and high-resolution TEM were also used to characterize the products. The obtained manganese oxides maintain the one-dimensional morphology similar to the precursor γ-MnOOH nanorods. Further experiments show that the as-prepared manganese oxide nanorods have catalytic effect on the oxidation and decomposition of the methylene blue (MB) dye with H2O2.