Abstract:Cryptomelane-type MnO2 nanomaterials with a-crystalline phase were prepared by heat treatment of the mixture of MnCO3 and potassium oxalate followed by acid treatment. The evolution of the crystalline phase and morphology from MnCO3 to cryptomelane was investigated by XRD, BET, SEM and TEM. Moreover, MnO2 in nanoparticle, nanorod and nanofiber shapes could be controlled by adjusting the reaction time and temperature in the acid-treatment step. MnO2 nanofibers demonstrated promoted catalytic activity and recyclability for the oxidative degradation of various organic dyes, tetracyclines and bisphenol A via peroxymonosulfate (PMS) activation. About 99% of RhB, AO7, MB, red 2 and bisphenol A at a concentration of 20–50 mg/L could be degraded over MnO2 nanofibers within 12 min. Furthermore, antibiotics, like tetracycline, chlortetracycline and oxytetracycline, and bisphenol A could be mineralized efficiently, and 69–81% TOC removal was obtained. Compared to MnO2 nanowires synthesized by the traditional method with KMnO4, MnO2 nanofibers showed enhanced surface area (102 m2/g), more labile lattice oxygen species and higher oxygen vacancy content, which might be responsible for the superior catalytic performances. The radical quenching test and EPR analysis proved that radical (O2−, SO4− and OH) and non-radical (1O2) processes both existed, and the latter dominantly contributed to the degradation. Based on kinetic study, the activation energy of MnO2 nanofibers/PMS for RhB degradation was only 10.55 kJ/mol, which was lower than that of MnO2 nanowires (16.80 kJ/mol). This study not only offered a new, simple and economical protocol for the scaled-up synthesis of nano-scale MnO2 materials, but also demonstrated its potential in water remediation.

Large-scale Synthesis of Β-Mno2 Nanorods and Their Rapid and Efficient Catalytic Oxidation of Methylene Blue Dye

Nanorods of Manganese Oxides: Synthesis, Characterization and Catalytic Application

Preparation of MnO_2 Nanorod and Its Catalytic Performance

Synthesis and Characterization of Single Crystalline Mnooh and Mno2 Nanorods by Means of the Hydrothermal Process Assisted with Ctab

Controlled Morphology of One-Dimensional Manganese Dioxide with Dramatic Enhancing Removal Efficiency to Heavy Metal Ions in Aqueous Solution

Facile and large-scale synthesis of single-crystalline manganese oxyhydroxide/oxide nanostructures

Bismuth-doped Manganese Molybdenum Bimetallic Oxide Nanorods As a Highly Efficient Nitrogen Reduction Catalyst

Synthesis and Formation Mechanism of Manganese Dioxide Nanowires/nanorods.

Manganese Oxyhydroxide And Oxide Nanofibers For High Efficiency Degradation Of Organic Pollutants

Synthesis and Photocatalytic Activity of Small-Diameter Zno Nanorods

Facile and template-free preparation of α-MnO2 nanostructures and their enhanced adsorbability

Synthesis of Nanosized MnOOH Via Solvothermal Route

Oxidative degradation of aqueous organic contaminants over shape-tunable MnO2 nanomaterials via peroxymonosulfate activation

Study on degradation of acid orange II in aqueous solution using one-dimensional MnO(2) nanorods

Controlled Preparation of Novel Manganese Oxide Nanocrystals and Dye Adsorption Property

Mesoporous manganese dioxide prepared by nano-casting: An efficient catalyst for of methyl orange and oxalic acid degradation in aqueous solution

Synthesis of Mn3O4 Octahedrons and Other Manganese-Based Nanostructures Through a Simple and Green Route

Synthesis and Characterization of Γ-Mnooh Nanorods with Tetragonal Prism Cross Section

Synthesis and Catalytic Performance of Manganese Oxide Octahedral Molecular Sieve Nanorods for Formaldehyde Oxidation at Low Temperature

β-MnO2 nanowires: A novel ozonation catalyst for water treatment

Shape‐ and Size‐Controlled Synthesis of Mn3O4 Nanocrystals at Room Temperature