Abstract:Manganese oxides with desired structure are controllably obtained through annealing MnCO3 precursors with required structures. The structures of MnCO3 precursors are determined by a "mesocrystal formation" process in an ionic liquid system of a choline chloride/urea (CU) mixture. Without addition of surfactants, only CU solvent and manganese chloride are needed in the reaction system, in which the CU acts as reaction medium as well as control agent for particle growth. A shape transformation of MnCO3 particles from well-defined rhombohedral mesocrystals to ellipsoidal polycrystal ensembles, and to nanoparticulate aggregates is observed when heating the reaction system for 4 h at 120, 150, and 180 °C, respectively. With a longer aging time at 120 °C, etching and disassembly of MnCO3 mesocrystals happened. The correlation between the microstructure and the underlying formation mechanism is highlighted. Porous and nanowire-like MnO(x) nanostructures are obtained through a facile thermal conversion process from the diverse MnCO3 precursors, which are demonstrated as effective and efficient adsorbents to remove organic waste (e.g. Congo red) from water. Significantly, the nanowire-like MnO(x) nanostructures obtained by annealing the MnCO3 mesocrystals at 300 °C for 4 h can remove about 95% Congo red in waste water at room temperature in only one minute, which is superior to the reported hierarchical hollow nanostructured MnO2.

Synthesis of Porous Manganese Oxides Bars Via A Hydrothermal-Decomposition Method

A Facile Template-Free Preparation of Porous Manganese Oxides by Thermal Decomposition Method

Self-assembled Flower-Like Hierarchical Spheres and Nanobelts of Manganese Oxide by Hydrothermal Method and Morphology Control of Them

Controlled Morphology of One-Dimensional Manganese Dioxide with Dramatic Enhancing Removal Efficiency to Heavy Metal Ions in Aqueous Solution

The Convenient Preparation of Porous CuO Via Copper Oxalate Precursor

Synthesis and electrochemical properties of hierarchically porous Fe 2 O 3

Synthesis And Electrochemical Properties Of Co Doped Mno2 Framework With Nanofibrous Structure

Synthesis and characterization of TiO2-pillared microporous manganese oxide

Endowing Manganese Oxide with Fast Adsorption Ability Through Controlling the Manganese Carbonate Precursor Assembled in Ionic Liquid.

Single Crystal Manganese Oxide Hexagonal Plates with Regulated Mesoporous Structures

Facile and large-scale synthesis of single-crystalline manganese oxyhydroxide/oxide nanostructures

Synthesis of Nanosized MnOOH Via Solvothermal Route

Nanorods of Manganese Oxides: Synthesis, Characterization and Catalytic Application

Synthesis of Large Mesoporous-Macroporous and High Pore Volume, Mixed Crystallographic Phase Manganese Oxide, Mn2O3/Mn3O4 Sponge

Porous manganese oxides synthesized with natural products at room temperature: a superior humidity-tolerant catalyst for ozone decomposition

Manganese Oxyhydroxide And Oxide Nanofibers For High Efficiency Degradation Of Organic Pollutants

Phase and Morphology Evolution of Manganese Oxides During Thermal Treatment

Synthesis And Characterization Of Porous Magnesium Hydroxide And Oxide Nanoplates

Formation and Conversion Mechanisms Between Single-Crystal Gamma-Mnooh and Manganese Oxides

Facile Synthesis Of Amorphous Mesoporous Manganese Oxides For Efficient Catalytic Decomposition Of Ozone

Shape‐ and Size‐Controlled Synthesis of Mn3O4 Nanocrystals at Room Temperature