Hollow-structured Conjugated Porous Polymer Derived Iron/Nitrogen-codoped Hierarchical Porous Carbons As Highly Efficient Electrocatalysts
Wenbei Zhang,Tianlu Cui,Lingyun Yang,Chao Zhang,Ming Cai,Sai Sun,Yefeng Yao,Xiaodong Zhuang,Fan Zhang
DOI: https://doi.org/10.1016/j.jcis.2017.02.061
IF: 9.9
2017-01-01
Journal of Colloid and Interface Science
Abstract:Iron and nitrogen (Fe/N) co-doped porous carbons have already shown great potential as electrocatalysts for oxygen reduction reaction in alkaline media. However, it still remains a great challenge to finely integrate a hierarchical porous structure and Fe/N co-doping effect into one material at the same time. In this work, a rational design toward Fe/N-codoped hierarchical porous carbon spheres was developed by the formation of an iron-porphyrin-containing conjugated microporous polymer sphere with hollow structure (HCMP) through a silica sphere template directed condensation of pyrrole and 1,4-phthalaldehyde, then etched with NaOH, and treated with FeCl2. The resulting HCMP-Fe polymer was readily converted to a series of Fe/N co-doped hierarchical porous carbons (HPC-Fe/N-X, X=700-900) upon pyrolysis at different temperatures and etching treatment. These porous carbons exhibit the high specific surface areas up to 518m2g-1 and the contents of N and Fe up to 3.28at.% and 0.85wt.%, respectively. Benefiting from the high surface area, Fe/N co-doping character, HPC-Fe/N-700 exhibited excellent electrochemical catalytic performance for oxygen reduction reaction under alkaline condition (0.1M KOH) with a low half-wave potential (0.84V), a dominant four-electron transfer mechanism (n=3.89 at 0.65V), as well as a high diffusion limiting current density (JL=5.19mAcm-2), comparable to those porous carbon-based ORR catalysts with excellent electrochemical performance.