Abstract:In response to the high cost of magnesium phosphate cement (MPC), due to the high production energy consumption of raw material MgO (sintering at 1600 °C for 5 h), and the requirement of adding retarders during the preparation process, we proposed using common elements B, Li, Na, K, and Cl in salt lakes to promote the sintering performance of MgO. We subsequently studied the preparation technology of low-activity MgO obtained from the pyrolysis of bischofite in salt lakes and low-temperature sintering (≤ 1200 °C). The migration law of coexisting elements and low-temperature sintering mechanism of salt lake bischofite was revealed during pyrolysis and low-temperature sintering, expanding the utilization path of salt lake bischofite and promoting resource recycling. We simultaneously developed a preparation technology for low-activity MgO used as raw MPC material, avoiding the use of retarders and reducing the raw material costs in the preparation of MPC. The results showed that coexisting elements migration was present in four different types of processes during the sintering process. Octahedral particles with a preferred orientation and exposed MgO (111) crystal face were obtained. With increased sintering temperature and time, the content and particle size of MgO increased and the specific surface area and porosity decreased, which led to the prolonged neutralization reaction time, as well as increased sintering degree and decrease in hydration activity. The formation of the liquid phase by bischofite and its coexisting elements was the key to MgO sintered at 1000 °C.

Preparation of Ccalcining MgO and its precursor

Synthesis of a Porous Nano‐CaO/MgO‐Based CO2 Adsorbent

Study on Preparation of MgO Crystal Whisker from Magnesite

Fabrication of Y2O3-doped MgO Refractory Raw Materials Based on Magnesium Hydroxide from Salt-Lake Brine

Regenerable MgO-based Sorbents for CO2 Capture at Elevated Temperature and Pressure: Experimental and DFT Study

Promotion of MgO Sorbents with Eutectic Carbonate Doping for High-Temperature and Pressure CO2 Capture

Research on preparation of high purity magnesite from MgCl2·6H2O

Preparation of Magnesium Hydroxide Chloride Hydrate Nanowires Using Calcined Dolomite

Preparation of Nanometer Magnesia with High Surface Area and Study on the Influencing Factors of the Preparation Process

Preparation and characterization of anhydrous magnesium carbonate: Effect of different anions of the magnesium sources

Preparation and Crystal Transformation Process of Magnesium Carbonate Hydrate Using MgSO4 as Raw Material

CO2 Adsorption Performance of Na/K-Impregnated MgO

A Technology of Preparing Honeycomb-Like Structure Mgo from Low Grade Magnesite

Development and Characterization on the Isothermal Kinetics of Mg(OH)2-sol Synthesized by Chemical Method

Synthesis of MgO powders by precipitant for transparent ceramics

Nanosized MgO Powder Preparation by Homogeneous Precipitation-Post Annealing Method Using Mg(NO3)2·6H2O as Raw Material

Exploration on influence of calcination temperature on structure and surface acidity and basicity of Mg(Al)O composite oxide

Preparation technology and microstructural changes of low-activity magnesium oxide based on salt lake bischofite

Preparation of Magnesium Hydroxide Dry Powder by Hydrating Method

The effects of solvent and microwave on the preparation of Magnesium Oxide Precursor: The effects of solvent and microwave on the preparation of Magnesium Oxide Precursor

Additives Applied for Preparation of Superfine Mg(Oh)(2) Particles by Light-Burned Mgo at Low Temperature