Abstract:Utilizing MgO as the precursor and deionized water as the solvent, this study synthesized nanoparticles of Mg(OH)2 via hydrothermal methods, aiming to control its purity, particle size, and morphology by understanding its growth under non-uniform nucleation. Characterization of crystal morphology and structure was conducted through scanning electron microscopy and X-ray diffraction, while laser particle size detection assessed the secondary particle size distribution. The study focused on how MgO's hydrothermal process conditions influence Mg(OH)2 crystal growth, particularly through ion concentration and release rate adjustments to direct crystal growth facets. These adjustments shifted the dominant growth plane, enhancing the peak intensity ratio I001/I101 from 1.03 to 2.14, thereby reducing surface polarity and secondary aggregation of crystals. The study of the physicochemical properties of the same sample at different times revealed the pattern of crystal dissolution and recrystallization. A 2 h hydrothermal reaction notably altered the particle size distribution, with a decrease in particles sized 0.2~0.4 μm and an increase in those sized 0.4~0.6 μm, alongside new particles over 1 μm, indicating a shift toward uniformity through dissolution and recrystallization. Optimal conditions (6% magnesium oxide concentration, 160 °C, 2 h) led to the synthesis of highly dispersed, uniformly sized magnesium hydroxide, showcasing a simple, eco-friendly, and high-yield process.

Solvothermal Synthesis of Mg(OH)2nanotubes Using Mg10(OH)18Cl2·5H2O Nanowires As Precursors

Synthesis of MgO nanotube bundles

The Preparation of Mg 3 Si 2 O 5 (OH) 4 Nanotubes under Solvothermal Conditions

The Preparation Of Mg3si2o5(Oh)(4) Naotubes Under Solvothermal Conditons

Solvothermal Synthesis of Coo, Co3o4, Ni(Oh)(2) and Mg(Oh)(2) Nanotubes

Synthesis of 3 Mg(OH)2·MgCl2·8H2O Nanowires from Mg(OH)2 Micro-Agglomerates

MgO nanostructures synthesized by thermal evaporation

Synthesis of MgO Nanowires Combined with C Nanotubes

Formation of rod-like Mg(OH)2 nanocrystallites under hydrothermal conditions and the conversion to MgO nanorods by thermal dehydration

Preparation of Magnesium Hydroxide Chloride Hydrate Nanowires Using Calcined Dolomite

Nanoscale magnesium hydroxide and magnesium oxide powders: Control over size, shape, and structure via hydrothermal synthesis

Gallium-assisted growth of flute-like MgO nanotubes, Ga<sub>2</sub>O<sub>3</sub>-filled MgO nanotubes, and MgO/Ga<sub>2</sub>O<sub>3</sub>co-axial nanotubes

Composite-hydroxide-assisted hydrothermal synthesis of magnesium silicate nanotube

Single-crystal MgS nanotubes: synthesis and properties

Investigation of Crystallization Growth Characteristics of Mg(OH)2 Crystals under Unconstrained Conditions

Microwave-assisted synthesis of fibre-like Mg(OH)2 nanoparticles in aqueous solution at room temperature

Synthesis and Characterization of Single Crystalline Mnooh and Mno2 Nanorods by Means of the Hydrothermal Process Assisted with Ctab

Synthesis of Magnesium Borate Nanorods by Sol-Gel Process

Preparation of Mg(Oh)(2) Nanorods

Synthesis and Characterization of MgO Single-Crystalline One-Dimensional Nanostructures

Synthesis of yttrium hydroxide and oxide nanotubes