Abstract:Utilizing MgO as the precursor and deionized water as the solvent, this study synthesized nanoparticles of Mg(OH)2 via hydrothermal methods, aiming to control its purity, particle size, and morphology by understanding its growth under non-uniform nucleation. Characterization of crystal morphology and structure was conducted through scanning electron microscopy and X-ray diffraction, while laser particle size detection assessed the secondary particle size distribution. The study focused on how MgO's hydrothermal process conditions influence Mg(OH)2 crystal growth, particularly through ion concentration and release rate adjustments to direct crystal growth facets. These adjustments shifted the dominant growth plane, enhancing the peak intensity ratio I001/I101 from 1.03 to 2.14, thereby reducing surface polarity and secondary aggregation of crystals. The study of the physicochemical properties of the same sample at different times revealed the pattern of crystal dissolution and recrystallization. A 2 h hydrothermal reaction notably altered the particle size distribution, with a decrease in particles sized 0.2~0.4 μm and an increase in those sized 0.4~0.6 μm, alongside new particles over 1 μm, indicating a shift toward uniformity through dissolution and recrystallization. Optimal conditions (6% magnesium oxide concentration, 160 °C, 2 h) led to the synthesis of highly dispersed, uniformly sized magnesium hydroxide, showcasing a simple, eco-friendly, and high-yield process.

Synthesis of 3 Mg(OH)2·MgCl2·8H2O Nanowires from Mg(OH)2 Micro-Agglomerates

Preparation of Magnesium Hydroxide Chloride Hydrate Nanowires Using Calcined Dolomite

Composition and Morphology of the Thermal Decomposition Products of 3mg(oh)2·mgcl2·8h2o Nanowires

Solvothermal Synthesis of Mg(OH)2nanotubes Using Mg10(OH)18Cl2·5H2O Nanowires As Precursors

Investigation of Crystallization Growth Characteristics of Mg(OH)2 Crystals under Unconstrained Conditions

Nanoscale magnesium hydroxide and magnesium oxide powders: Control over size, shape, and structure via hydrothermal synthesis

Synthesis of Mg(Oh)(2) Nanoparticles from Mgo Using Magnesium Acetate As Additive

Magnesium Nitrate As Additive for Synthesis of Mg(OH)2 Nanoparticles

Synthesis of MgO nanotube bundles

Microwave-assisted synthesis of fibre-like Mg(OH)2 nanoparticles in aqueous solution at room temperature

Controllable Synthesis of Mg(OH) 2 Whiskers Using 5Mg(OH) 2 ·MgSO 4 ·2H 2 O Whiskers with Tunable Diameter as Precursors

Controllable Synthesis of Magnesium Oxysulfate Nanowires with Different Morphologies

Formation of rod-like Mg(OH)2 nanocrystallites under hydrothermal conditions and the conversion to MgO nanorods by thermal dehydration

Preparation and thermal decomposition of 5Mg(OH)2·MgSO4·2H2O nanowhiskers

MgO nanostructures synthesized by thermal evaporation

Synthesis of MgO Nanowires Combined with C Nanotubes

Hydrothermal Synthesis and Characterization of One-dimensional Magnesium Hydroxide Chloride Hydrate in CaO-MgCl<SUB>2</SUB>-H<SUB>2</SUB>O System: Hydrothermal Synthesis and Characterization of One-dimensional Magnesium Hydroxide Chloride Hydrate in CaO-MgCl<SUB>2</SUB>-H<SUB>2</SUB>O System

Hydrothermal Synthesis and Characterization of One-dimensional Magnesium Hydroxide Chloride Hydrate in CaO-MgCl_2-H_2O System

Hydrothermal Synthesis And Characterization Of One-Dimensional Magnesium Hydroxide Chloride Hydrate In Cao-Mgcl2-H2o System

Synthesis of High Surface Area Nanometer Magnesia by Solid-State Chemical Reaction

Preparation of highly-dispersed Mg(OH)2 powders and influence factors