Superstructured magnesium hydroxide sulfate hydrate fibres Photoluminescence study
yi ding,huazhang zhao,yugang sun,guangtao zhang,hao wu,yitai qian
DOI: https://doi.org/10.1016/S1466-6049(00)00105-7
2001-01-01
International Journal of Inorganic Materials
Abstract:Magnesium hydroxide sulfate hydrates (MHSHs), first Either the unusual superstructure or the domains may discovered in nature in a submarine geothermal system in predict that it is of possible value to both fundamental and 1978, have now been accepted as crucial minerals which applied research, thus we carried out the photolumineschave a profound effect on the geochemical cycle process ence study of this sample which is the main topic of this [1‐3]. Since several members of the MHSH family, e.g., manuscript. In order to investigate the conditions necessary 5Mg(OH) ?MgSO ?3H O (5‐1‐3 phase), 3Mg(OH) ? to obtain pure MHSH fibres, sodium hydroxide was used 24 2 2 MgSO ?8H O (3‐1‐8 phase), were shown to have good here instead of aqueous ammonia. 42 strength for building materials, the MgO?MgSO ?H O The MHSH fibres studied here were prepared using the 42 system has also become an attractive subject of numerous conventional hydrothermal method at temperature range of investigations in the ceramic field [4‐6]. Iwanaga [7‐9] 150‐180 8C. Below 1108C, only Mg(OH) with a hexagon2 ever measured the Young’s modulus of the MHSH fibres al plate shape was produced. From 120 to 1408C, through a fine tensile experiment which demonstrated their Mg(OH) and MHSH fibres coexisted. Above 150 8C, pure 2 potential application value as reinforcements of composite MHSH fibres could be obtained. These fibres had a materials. In spite of the fact that several MHSH samples chemical composition of Mg(OH) :MgSO :H O of 24 2