Abstract:Utilizing MgO as the precursor and deionized water as the solvent, this study synthesized nanoparticles of Mg(OH)2 via hydrothermal methods, aiming to control its purity, particle size, and morphology by understanding its growth under non-uniform nucleation. Characterization of crystal morphology and structure was conducted through scanning electron microscopy and X-ray diffraction, while laser particle size detection assessed the secondary particle size distribution. The study focused on how MgO's hydrothermal process conditions influence Mg(OH)2 crystal growth, particularly through ion concentration and release rate adjustments to direct crystal growth facets. These adjustments shifted the dominant growth plane, enhancing the peak intensity ratio I001/I101 from 1.03 to 2.14, thereby reducing surface polarity and secondary aggregation of crystals. The study of the physicochemical properties of the same sample at different times revealed the pattern of crystal dissolution and recrystallization. A 2 h hydrothermal reaction notably altered the particle size distribution, with a decrease in particles sized 0.2~0.4 μm and an increase in those sized 0.4~0.6 μm, alongside new particles over 1 μm, indicating a shift toward uniformity through dissolution and recrystallization. Optimal conditions (6% magnesium oxide concentration, 160 °C, 2 h) led to the synthesis of highly dispersed, uniformly sized magnesium hydroxide, showcasing a simple, eco-friendly, and high-yield process.

Formation of rod-like Mg(OH)2 nanocrystallites under hydrothermal conditions and the conversion to MgO nanorods by thermal dehydration

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

MgO nanostructures synthesized by thermal evaporation

Investigation of Crystallization Growth Characteristics of Mg(OH)2 Crystals under Unconstrained Conditions

Nanoscale magnesium hydroxide and magnesium oxide powders: Control over size, shape, and structure via hydrothermal synthesis

Synthesis and Characterization of Single Crystalline Mnooh and Mno2 Nanorods by Means of the Hydrothermal Process Assisted with Ctab

A Simple and Novel Low-Temperature Hydrothermal Synthesis of ZnO Nanorods

Preparation of Magnesium Hydroxide Chloride Hydrate Nanowires Using Calcined Dolomite

Preparation of Mg(Oh)(2) Nanorods

Morphology Preservation and Crystallinity Improvement in the Thermal Conversion of the Hydrothermal Synthesized Mgbo2(Oh) Nanowhiskers to Mg2b2o5 Nanowhiskers

Solvothermal Synthesis of Mg(OH)2nanotubes Using Mg10(OH)18Cl2·5H2O Nanowires As Precursors

Preparation and Characterization of Mg(OH) 2 Nanorods by Liquid–solid Arc Discharge Technique

Preparation and characterization of lamellar-like Mg(OH)2 nanostructures via natural oxidation of Mg metal in formamide/water mixture

Sequential Occurrence of ZnO Nanopaticles, Nanorods, and Nanotips During Hydrothermal Process in a Dilute Aqueous Solution

H2SO4-assisted hydrothermal preparation of γ-AlOOH nanorods

Synthesis and Characterization of MgO Single-Crystalline One-Dimensional Nanostructures

Hydrothermal conversion of magnesium oxysulfate whiskers to magnesium hydroxide nanobelts

Preparation and thermal decomposition of 5Mg(OH)2·MgSO4·2H2O nanowhiskers

Direct Observation of the Growth Process of MgO Nanoflowers by a Simple Chemical Route.

Synthesis Of Yttrium Oxide Hydroxide Nitrate Nanorods By Hydrothermal Method

Large-scale synthesis of single-crystalline MgO with bone-like nanostructures