Abstract:Mesoporous metal oxides with wide pore size, high surface area, and uniform porous structures have demonstrated excellent advantages in various fields. However, the state-of-art synthesis approaches are dominated by wet chemistry, accompanied by use of excessive solvent, and the requirement of time-consuming drying process. Herein, we report a mechanochemical solid-state route to synthesize mesoporous Al2O3 (meso-Al2O3) via aluminum isopropoxide-copolymers assembly. The obtained meso-Al2O3 shows a record high surface area (similar to 644 m(2) g(-1)) and narrow pore size distribution (centered at similar to 5 nm). Moreover, a mechanochemical nonhydrolytic sol-gel strategy is introduced to fabricate mesoporous metal (Cu, Co, Mn, Fe, Mg, Ni)-aluminum binary oxide by using anhydrous metal chlorides and aluminum isopropoxide interplay. More importantly, four or five metals-aluminum oxide complexes with abundant mesopores and single cubic crystalline phase known as high-entropy ceramics are produced. To the best of our knowledge, mesoporous high-entropy metal oxides have not been prepared before, because the high crystallization temperature would make mesopores collapse. Additionally, this high-entropy property endows (CuNiFeCoMg)O-x-Al2O3 with superior SO2-resisting performance (1000 ppm of SO2 in N-2 at 280 degrees C) in the catalytic oxidation of CO compared to single CuO-Al2O3.

A simple solution calcination route to porous MgO nanoplates

Synthesis of a Porous Nano‐CaO/MgO‐Based CO2 Adsorbent

Simple Synthesis of Single-crystalline Nanoplates of Magnesium Oxide

A Vacuum Calcination Route to High-Surface-area MgO Nanoplates for Superior Arsenate Adsorption and Catalytic Properties

Synthesis And Characterization Of Porous Magnesium Hydroxide And Oxide Nanoplates

Mechanochemical Nonhydrolytic Sol–Gel-Strategy for the Production of Mesoporous Multimetallic Oxides

Synthesis of Porous Manganese Oxides Bars Via A Hydrothermal-Decomposition Method

Large-scale synthesis of single-crystalline MgO with bone-like nanostructures

Synthesis of High Surface Area Nanometer Magnesia by Solid-State Chemical Reaction

MgO nanostructures synthesized by thermal evaporation

Self-assembly of porous MgO nanoparticles into coral-like microcrystals

General Solution Route for Nanoplates of Hexagonal Oxide or Hydroxide

(NaPO3)6-assisted wet formation of dispersive Mg(OH)2 nanoplates

Preparation of Nanometer Magnesia with High Surface Area and Study on the Influencing Factors of the Preparation Process

Direct Observation of the Growth Process of MgO Nanoflowers by a Simple Chemical Route.

Synthesis of MgO Microspheres with Nanosheets in a Mechanical Force Reactor and Its Optical Property

Preparation of Ccalcining MgO and its precursor

Nanosized MgO Powder Preparation by Homogeneous Precipitation-Post Annealing Method Using Mg(NO3)2·6H2O as Raw Material

Facile and rapid synthesis of nanoplates Mg(OH)2 and MgO via Microwave technique from metal source: structural, optical and dielectric properties

Nanoscale magnesium hydroxide and magnesium oxide powders: Control over size, shape, and structure via hydrothermal synthesis

Magnesium Nitrate As Additive for Synthesis of Mg(OH)2 Nanoparticles