Abstract:Utilizing MgO as the precursor and deionized water as the solvent, this study synthesized nanoparticles of Mg(OH)2 via hydrothermal methods, aiming to control its purity, particle size, and morphology by understanding its growth under non-uniform nucleation. Characterization of crystal morphology and structure was conducted through scanning electron microscopy and X-ray diffraction, while laser particle size detection assessed the secondary particle size distribution. The study focused on how MgO's hydrothermal process conditions influence Mg(OH)2 crystal growth, particularly through ion concentration and release rate adjustments to direct crystal growth facets. These adjustments shifted the dominant growth plane, enhancing the peak intensity ratio I001/I101 from 1.03 to 2.14, thereby reducing surface polarity and secondary aggregation of crystals. The study of the physicochemical properties of the same sample at different times revealed the pattern of crystal dissolution and recrystallization. A 2 h hydrothermal reaction notably altered the particle size distribution, with a decrease in particles sized 0.2~0.4 μm and an increase in those sized 0.4~0.6 μm, alongside new particles over 1 μm, indicating a shift toward uniformity through dissolution and recrystallization. Optimal conditions (6% magnesium oxide concentration, 160 °C, 2 h) led to the synthesis of highly dispersed, uniformly sized magnesium hydroxide, showcasing a simple, eco-friendly, and high-yield process.

Self-assembly of porous MgO nanoparticles into coral-like microcrystals

A simple solution calcination route to porous MgO nanoplates

Magnesium catalyzed growth of SiO2 hierarchical nanostructures by a thermal evaporation process

Large-scale synthesis of single-crystalline MgO with bone-like nanostructures

MgO nanostructures synthesized by thermal evaporation

Hierarchical porous structures by using zeolite nanocrystals as building blocks

Self-assembled Growth of MgO Nanosheet Arrays Via a Micro-Arc Oxidation Technique

Preparation of Magnesium Hydroxide Chloride Hydrate Nanowires Using Calcined Dolomite

Direct Observation of the Growth Process of MgO Nanoflowers by a Simple Chemical Route.

TEMPLATE-INDUCED MORPHOLOGICAL PRESERVATION AND SELF-ASSEMBLY OF NONPOROUS MGO NANOSTRUCTURES DURING THE DECOMPOSITION OF NANOSCALE MG(OH)2 PRECURSORS

Synthesis of MgO Microspheres with Nanosheets in a Mechanical Force Reactor and Its Optical Property

Preparation and characterization of lamellar-like Mg(OH)2 nanostructures via natural oxidation of Mg metal in formamide/water mixture

Facile preparation and characterisation of magnesium hydroxide assembly spheres

Synthesis And Characterization Of Porous Magnesium Hydroxide And Oxide Nanoplates

Microwave-assisted synthesis of fibre-like Mg(OH)2 nanoparticles in aqueous solution at room temperature

Investigation of Crystallization Growth Characteristics of Mg(OH)2 Crystals under Unconstrained Conditions

A Simple Route for the Synthesis of Coral-Like Accretion of Hollow Carbon Microspheres with Thin Walls

Photolysis-Induced Mineralization of Self-Assembled Witherite Hierarchical Architectures

Biomineralization of Varied Calcium Carbonate Crystals by the Synergistic Effect of Silk Fibroin/magnesium Ions in a Microbial System

Kinetics-driven growth of orthogonally branched single-crystalline magnesium oxide nanostructures.

In Vitro Synthesis of High Mg Calcite under Ambient Conditions and Its Implication for Biomineralization Process