Abstract:Magnesium oxysulfate (MOS) whiskers are commonly synthesized through a dissolution-precipitation mechanism, wherein Mg(OH) 2 dissolves to form Mg(OH) 6 4- , followed by reactions with SO 4 2- and H 2 O to yield MOS whiskers. However, the impact of Mg(OH) 2 precursor properties on the formation process of MOS whiskers has been insufficiently explored, and sector-like and needle-like morphologies were both observed in previous studies. In this study, we systematically investigated how the properties of Mg(OH) 2 precursors influenced the crystalline structure and morphology of MOS whiskers. Under various experimental conditions, MgSO 4 ·5Mg(OH) 2 ·2H 2 O (152MOS) whiskers were consistently obtained, regardless of Mg(OH) 2 morphology and size. The size of Mg(OH) 2 emerged as a critical factor in shaping the morphology of 152MOS whiskers. Smaller-sized Mg(OH) 2 (≤106±37 nm) favored the formation of sector-like whiskers, while larger-sized Mg(OH) 2 (≥206±98 nm) encouraged the development of needle-like whiskers. This distinction was attributed to the slower dissolution rate exhibited by larger-sized Mg(OH) 2 , maintaining a smaller number of 152MOS nuclei and promoting the growth of needle-like whiskers instead of the aggregation of 152MOS nuclei into sector-like structures. In addition, the effects of the molar ratio of Mg 2+ to SO 4 2- and hydrothermal temperature were also studied. The average length and diameter of the needle-like whiskers prepared with Mg(OH) 2 of 331±145 nm under optimized conditions were 77±32 and 0.39±0.10 μm, respectively. This study presented an effective strategy for controlling the morphology of 152MOS whiskers.

Hydrothermal synthesis of whisker-like magnesium borate hydroxide (MgBO2(OH)) nanoflakes

Hydrothermal Synthesis and Characterization of Magnesium Borate Hydroxide Nanowhiskers

Influence of process parameters on hydrothermal formation of magnesium borate hydroxide nanowhiskers

Study on Preparation of MgO Crystal Whisker from Magnesite

Morphology Preservation and Crystallinity Improvement in the Thermal Conversion of the Hydrothermal Synthesized Mgbo2(Oh) Nanowhiskers to Mg2b2o5 Nanowhiskers

Green, Noncorrosive, Easy Scale-Up Hydrothermal–Thermal Conversion: A Feasible Solution to Mass Production of Magnesium Borate Nanowhiskers

Flux-Assisted Thermal Conversion Route To Pore-Free High Crystallinity Magnesium Borate Nanowhiskers At A Relatively Low Temperature

Hydrothermal formation and characterization of magnesium oxysulfate whiskers

Preparation of Magnesium Hydroxide Chloride Hydrate Nanowires Using Calcined Dolomite

Hydrothermal Formation of the Head-to-Head Coalesced Szaibelyite MgBO 2 (OH) Nanowires

Nanoscale magnesium hydroxide and magnesium oxide powders: Control over size, shape, and structure via hydrothermal synthesis

Synthesis of Magnesium Borate Nanorods by Sol-Gel Process

Hydrothermal Mass Production of MgBO2(OH) Nanowhiskers and Subsequent Thermal Conversion to Mg2B2O5 Nanorods for Biaxially Oriented Polypropylene Resins Reinforcement

Preparation and thermal decomposition of 5Mg(OH)2·MgSO4·2H2O nanowhiskers

Hydrothermal Synthesis Process of Magnesium Oxysulfate Whiskers

Controllable Synthesis of Mg(OH) 2 Whiskers Using 5Mg(OH) 2 ·MgSO 4 ·2H 2 O Whiskers with Tunable Diameter as Precursors

Hydrothermal conversion of magnesium oxysulfate whiskers to magnesium hydroxide nanobelts

Hydrothermal formation of magnesium oxysulfate whiskers in the presence of ethylenediaminetetraacetic acid

Formation of rod-like Mg(OH)2 nanocrystallites under hydrothermal conditions and the conversion to MgO nanorods by thermal dehydration

Synthesis Of Magnesium Oxysulfate Whiskers In The Presence Of Sodium Dodecyl Benzene Sulfonate

Effects of the properties of Mg(OH) 2 precursor on the hydrothermal synthesis of magnesium oxysulfate whiskers