Abstract:In current work, Cu-20wt%W (Cu-20W) composite of near theoretical density (99.69 %) and high electrical conductivity (86.78 %IACS) was fabricated by spray drying technique and hot isostatic pressing (HIP), aiming to enhance the mechanical properties of Cu-W composite while maintaining high conductivity. The impacts of W nanoparticles on the microstructure and properties of Cu-20W samples were evaluated. Adding W nanoparticles can remarkably refine the grain of Cu and strengthen the Cu-W composite through a pinning effect. Room temperature tensile strength and compressive yield strength of Cu-20W composite were 380 MPa and 304.49 MPa, which are 117.14 % and 616.95 % higher than that of pure Cu (175 MPa and 42.47 MPa), respectively. Tungsten nanoparticles can promote the high-temperature reliability of Cu-W samples. Tensile strength of pure Cu and Cu-20W sample gradually decreased with increasing test temperature, but the percentage increment of tensile strength increased. The tungsten particles pinned at grain boundaries during hot deformation inhibit recrystallization grain growth and hinder dislocation movement, thereby contributing to the high-temperature properties of Cu-20W composite. The peak stress of Cu-20W sample is 146.60 % higher than pure Cu, even at close to the melting point of Cu (940 °C). The strength of Cu-20W composite is heightened by combining fine-grain strengthening and dispersion strengthening due to the introduced W nanoparticles.

Fabrication of 60 wt%W-40 wt%Cu composite with crystal orientation by combustion synthesis and melt-infiltration in ultrahigh-gravity field

Fabrication of Cu-riched W-Cu composites by combustion synthesis and melt-infiltration in ultrahigh-gravity field

Study of a New Method to Fabricate W–Cu Composites

Tungsten Joining with Copper Alloy and Its High Heat Load Performance

In Suit Synthesis and Bonding of Cu to W–Cu Composite by Combustion Synthesis and Centrifugal Infiltration

Fast fabrication of W-Cu functionally graded material by high-gravity combustion synthesis and melt-infiltration

Fabrication of W–Cu Functionally Graded Material with Improved Mechanical Strength

Interfacial Regulation and Fracture Mechanism of Al–Si/SiC Composites Infiltrated under Super-Gravity Field

Microstructural studies of W–10wt.% Cu composites prepared by using ultrafine composite powder

Microstructure and high-temperature mechanical properties of Cu-W composite prepared by hot isostatic pressing

Fabrication and microstructure of W/Cu functionally graded material

Enhanced mechanical properties and thermal conductivity of W-30Cu composite fabricated with monodisperse and nearly spherical W powder

Interfacial Failure Mechanism in Tungsten Fiber Reinforced Copper-Based Composites Fabricated by Combustion Synthesis Melt Infiltration under Ultra-High Gravity

Research on the densification of W–40 wt.%Cu by liquid sintering and hot-hydrostatic extrusion

Combustion Synthesis of TiB2-TiC/42CrMo4 Composites with Gradient Joint Prepared in Different High-Gravity Fields

Tungsten Copper Composite Fabricated by Compound Plastic Deformation Technologies

Effect of sintering temperature on fine-grained Cu W composites with high copper

Preparation of WC/CoCrFeNiAl0.2 high-entropy-alloy composites by high-gravity combustion synthesis

Microstructure and Properties of W Cu Composites with Low Copper Content at Different Sintering Temperatures

Freeze-casted tungsten skeleton reinforced copper matrix composites

High-gravity Combustion Synthesis of W-Cr Alloys with Improved Hardness