Abstract:A Zn-Sn coating of ~30 μm thickness was prepared on an iron substrate by mechanical deposition using zinc and tin powders as raw materials. The Zn-Sn coating consists of zinc powder particles physically stacked with tin powder particles and filled with reduced tin, and the tin content in the coating is 20%–30%. The resulting Zn-Sn coating was characterized and analyzed with scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), polarization curves (Tafel), electrochemical impedance (EIS), and energy dispersive X-ray spectrometry (EDS). The results showed that the Zn powder was co-deposited with the Sn powder in a portable manner and the Sn powder was deflected and deformed to a great extent. The spot-flocculated reduced Sn also covered the surface of the Zn powder to fill the interstices of the coating to make the coating more compact. Compared with the pure Zn coating, the Zn-Sn coating has a positive shift of 68 mV in the self-corrosion potential in the polarization test, and the corrosion current was only 20% of that of the pure Zn coating. The reduced Sn had a shielding effect on the Zn powder and at the same time, in combination with inert tin powder, the polarization resistance of the plated layer increased to 1118 Ω/cm2. Furthermore, compared to the pure zinc layer, the time of white rust and red rust increased by 24 and 240 h, respectively. In addition, the XPS results showed that the Zn-Sn plating layer was clearly passivated, which was mainly due to the formation of Zn(OH)2 and Sn(OH)2. The results also emphasized that the tin element in the Zn-Sn plated layer can maintain the morphology of zinc powder, compact the plating layer, and prevent the release of corrosion products, thus improving the corrosion resistance of the Zn-Sn coating.

Influence of intermittent air introduction on formation of Zn films by mechanical coating technique

Influence of Surface Modification of Metallic Substrate on In-Situ Growth and Adhesion Strength of ZSM-5 Films

Influence of Metal Properties on the Formation and Evolution of Metal Coatings During Mechanical Coating

Fabrication of Zinc Coatings on Alumina Balls from Zinc Powder by Mechanical Coating Technique and the Process Analysis

Atomic Layer Deposition of Zinc Oxide Films: Effects of Nanocrystalline Characteristics on Tribological Performance

Growth Temperature Dependent Evolutions of Microstructural, Optical and Magnetic Properties of Zn0.75Co0.25O Films

The influence of the processing parameters on the formation of iron thin films on alumina balls by mechanical coating technique

Study on Microstructure and Properties of Mechanically Deposited Zn-Sn Coating

Inter-Diffusion of Mg and Zn in Vacuum-Evaporated Mg Films on Zn Coated Steel Substrates

Influence of Annealing on Microstructure and Magnetic Properties of Co-Sputtered Co-doped ZnO Thin Films

Friction mechanism of zinc oxide films prepared by atomic layer deposition

Influence of Postdeposition Annealing on Crystallinity of Zinc Oxide Films

Influence of ZrB2 Nanoparticles on Microstructure and Mechanical Properties of Ni-Co Coating

The Preparation and Characterization of ZnO Films by in Situ Oxidation of Zn Films

Growth and Annealing of Zn-Mg Alloy Thick Films on Steel

Ordered ultra thin ZnO films on metal substrate

Effects of Annealing at Ar Ambient on the Physical Properties of Zn0.66Co0.34O Thin Film

Influence Of Processing Parameters On The Orientation And Microstructure Of Zn0.88ni0.02li0.10o Film

Influence of solution concentrations on surface morphology and wettability of ZnO thin films

Fabrication and characterization of zinc-coated aluminum particle joining materials via zincate treatment

S0430204 Formation and Its Process Analysis of Metal Films by Mechanical Coating Technique