Microwave Dielectric Properties of BaO–2(1 − X)zno–xnd2o3–4tio2 (x = 0–1.0) Ceramics

Shengquan Yu,Shuren Zhang,Bin Tang,Xiaohua Zhou,Youwei Fang

DOI: https://doi.org/10.1016/j.ceramint.2011.07.050

IF: 5.532

2011-01-01

Ceramics International

Abstract:Microwave dielectric properties of (1−x)BaZn2Ti4O11–xBaNd2Ti4O12 (x=0–1.0) ceramics were investigated by the solid-state reaction with the purpose of finding a microwave ceramics with high dielectric constant (ɛr), high quality factor (Q×f) and low temperature coefficient of resonant frequency (τf). A two phase system BaZn2Ti4O11–BaNd2Ti4O12 was formed and SEM photographs show equiaxed BaZn2Ti4O11 grains and columnar BaNd2Ti4O12 grains. The microwave dielectric properties were strongly determined by the chemical composition. As increasing x from 0 to 1.0, the phase composition varied from pure BaZn2Ti4O11, to the two phase system BaZn2Ti4O11–BaNd2Ti4O12 and then to pure BaNd2Ti4O12. Therefore, the ɛr raised from 29.1 to 82.0 and the Q×f values decreased from 54,630GHz to 8110GHz, and the τf values increased from −29ppm/°C to 94ppm/°C. 0.8BaZn2Ti4O11–0.2BaNd2Ti4O12 ceramics sintered at 1250°C for 2.5h had ɛr=39.1, Q×f=37,850GHz and τf=−9ppm/°C.