Microwave dielectric properties of (Zn1−xMgx)Nb2O6 ceramics

YingChun Zhang,ZhenXing Yue,ZhiLun Gui,LongTu Li

DOI: https://doi.org/10.1016/S0167-577X(03)00357-4

IF: 3

2003-01-01

Materials Letters

Abstract:Dielectric ceramics comprised of (Zn1−xMgx)Nb2O6 (x=0–1) with promising microwave properties were prepared by solid ceramic route. (Zn1−xMgx)Nb2O6 solid solutions exhibited columbite crystal structure for all compositions. The dielectric properties in this system exhibited a significant dependence on the sintering condition and composition of ceramics. The dielectric constant of (Zn1−xMgx)Nb2O6 ceramics increased with increasing relative densities for each x value. On the other hand, the dielectric constant of (Zn1−xMgx)Nb2O6 ceramics decreased from 23.66 to 19.7 as x value ranged from 0 to 1.0. The quality factors (Q×f) of (Zn1−xMgx)Nb2O6 ceramics increased with increasing sintering temperature, after reached the maximum values, then decreased. The highest Q×f values of sintered ceramics changed nonlinearly and ranged from 81,220 to 33,112 GHz. The τf showed a relative low value compared with those of ZnNb2O6 and MgNb2O6 and ranged from −29.46 to −70.56 ppm/°C. The τf was improved at x=0.5 and was −29.46 ppm/°C.