Microwave dielectric ceramics in (Ca1−xBax)(Zn1/3Nb2/3)O3 system

D. Liu,X.M. Chen,X. Hu

DOI: https://doi.org/10.1016/j.matlet.2006.06.077

IF: 3

2007-01-01

Materials Letters

Abstract:(Ca1−xBax)(Zn1/3Nb2/3)O3 (x=0–1.0) microwave dielectric ceramics were prepared and investigated. The Ba(Zn1/3Nb2/3)O3-based solid solution was observed for x=0.9, and the compositions with x=0.1–0.7 resulted in the mixture of two phases. Dielectric constant εr and temperature coefficient of resonant frequency τf of the present ceramics varied anomalously and reached their maximum at x=0.7–0.9, and these phenomena were originated from the partial substitution of small Ca2+ ions for larger Ba2+ at A-site. On the other hand, a good combination of microwave dielectric properties (εr=36, Qf=16,170 GHz, τf=−12 ppm/°C) were obtained at x=0.1, while the decreased Qf value was observed in other compositions.