High-ε Microwave Dielectrics in Pb<sub>0.6</sub>Ca<sub>0.4</sub>Zr<sub>0.6+x</sub>(Fe<sub>1/2</sub>Nb<sub>1/2</sub>)<sub>0.4-x</sub>O<sub>3</sub>System

xiandong hu,xiang ming chen
DOI: https://doi.org/10.1023/B:JECR.0000037724.17768.e4
2004-01-01
Journal of Electroceramics
Abstract:Modification of Pb0.6Ca0.4Zr0.6(Fe1/2Nb1/2)0.4O3 dielectric ceramics was performed by Zr substitution for (Fe, Nb). The XRD patterns showed that the single phase with orthorhombic distortion unit cell was obtained in the present ceramics. The decreasing dielectric constant by Zr substitution was due to its smaller value of α/r3ion. The calculated polarizability was compared with the observed one, and the results showed a good fit, considering the polarizability of oxygen dependent on the Vox. The Zr substitution on B-site reduced the temperature coefficient of dielectric constant effectively due to the reduced dielectric constant. The effects of tilting transition on the temperature coefficient of dielectric constant were also discussed. The modified microwave dielectric properties were obtained in Pb0.6Ca0.4Zr0.6+x(Fe1/2Nb1/2)0.4−xO3 for x = 0.3: ε r = 100, Q × f = 3,300 to 3,600 GHz, τ f = 6–8 ppm/°C.
What problem does this paper attempt to address?