Abstract:Vanadium carbide (VC) is extensively employed as a reinforcing agent in coating materials and a grain refiner in hard alloys, owing to its exceptional mechanical properties. A series of bulk VC ceramics were fabricated via high-temperature high-pressure sintering, followed by a comprehensive and systematic investigation of various properties of the sintered samples. The results revealed significant influences of processing temperature on the properties of sintered VC at 5.0 GPa. However, the exact nature of temperature dependence varied depending on the specific property. It was found that VC ceramics sintered at 1100 °C and 5.0 GPa exhibited the best overall performance, providing a relatively optimal temperature condition for synthesis. The Vickers hardness of the material reached an astonishing 43.2 GPa under a 9.8 N load, placing it within the category of superhard materials. However, the sintered sample exhibited a gradually lower hardness value of 30.4 GPa under a higher load of 29.4 N. Highly dense with a relative density of 99.8%, exhibiting near full density, the vanadium carbide ceramics possess an impressive Young's modulus of 544 GPa, indentation fracture resistance of 5.4 MPa m 1/2 , and an oxidation initiation temperature of 758 °C. This study offers practical guidance for the design of novel transition metal carbide superhard materials and provides valuable insights for the exploration of visualizing directions in the next generation of superhard materials.

A new method of synthesizing ultrafine vanadium carbide by dielectric barrier discharge plasma assisted milling

One-step synthesis of ultrafine WC–10Co hardmetals with VC/V 2 O 5 addition by plasma assisted milling

A Novel Method for Direct Synthesis of WC-Co Nanocomposite Powder

A Novel Approach to the Rapid in Situ Synthesis of Tungsten Carbide Nanopowder by Plasma Milling and Carbothermal Reduction

Synergism of Mechanical Milling and Dielectric Barrier Discharge Plasma on the Fabrication of Nano-Powders of Pure Metals and Tungsten Carbide

A Chemical Co-Reduction Route to Synthesize Nanocrystalline Vanadium Carbide

Dielectric Barrier Discharge Plasma Assisted Ball Milling Technology and Its Applications in Materials Fabrication

Mechanisms and mechanical properties of high-temperature high-pressure sintered vanadium carbide ceramics

Enhancement of the mechanical properties of ultrafine-grained WC-Co cemented carbides via the in-situ generation of VC

Influence of vanadium content on the microstructural evolution and mechanical properties of (TiZrHfVNbTa)C high-entropy carbides processed by pressureless sintering

Low-temperature synthesis of nanocrystalline vanadium diboride

Combustion Synthesis of VC/Fe Composites under the Action of an Electric Field

Influence of Vanadium Precursor Powder Size on Microstructures and Properties of W–V Alloy

Rapid synthesis of ultrafine WC-Co cemented carbides by in-situ reactions and spark plasma sintering

Diamond-Like Carbon Thin-Film Deposition Using A Magnetically Confined Rf Pecvd System

Novel high-performance polycrystalline diamond compact enhanced using vanadium additives

Preparation Technology of Ultra-Fine Tungsten Carbide Powders: an Overview

Ultrafine WC-Ni cemented carbides fabricated by spark plasma sintering

A Comparative Study about Production of Va nadium Carbide via Self Propagating High Temperature Synthesis and Reduction

Phase controlled synthesis of transition metal carbide nanocrystals by ultrafast flash Joule heating

Ultrafine grained WC-10FeCoCu cemented carbides doped with La 2 O 3 prepared by spark plasma sintering