Abstract:In 2011, a serious nuclear accident occurred in Fukushima, Japan, and one of the major causes was the destruction of the cladding material mainly made of Zr alloy due to a violent chemical reaction with high-temperature water vapor. Since then, scholars in various countries have been trying to find a better nuclear fuel cladding material. Because of its high temperature strength, ferritic/martensitic(F/M) steel is used in thermal power units. Over the past hundred years, the high temperature performance of ferritic/martensitic steel has developed simultaneously with the operating temperature of thermal power system. F/M steel is widely used in nuclear power system as well as thermal power, The fatigue life of nuclear fuel cladding material is an important parameter to study its service life, due to the special shape of the cladding material, especially for the pipe with a thickness of less than 0.5mm, it is difficult to directly measure its mechanical properties, this paper through special experimental materials and fixtures F/M pipe steel at room temperature and high temperature tensile test, as well as low cycle fatigue performance test, and its fracture port, surface crack analysis. Through the analysis and processing of experimental data, typical stress-cycle life curves, total strain amplitude-life curves, elastic strain amplitude-life curves, hysteresis curves with different strain amplitudes, and fatigue life prediction curves were obtained.

State analysis on reactor furnace pipe used over a design cycle

State Analysis on the Main Components of Reformer Furnace Pipe Used for A Design Cycle

State Analysis and Life Evaluation on Reformer Furnace Pipe Used for 100000Hrs

Microstructure and Property Analysis of Furnace Pipe Used over a Design Cycle

Experimental and simulative failure analysis of reformer furnace outlet manifolds serviced in aromatic plant

Corrosion Failures of High Temperature Heat Pipes

Cause Analyses of the Weld Seam Cracks of a Prehydrogenating Reactor

Cause Analysis and Improvement Measures for Pipeline Cracking of 9Cr-1Mo Material

Analysis on a Burst High-Temperature-Reheater Pipe in a Power Plant

SIMULATION AND ANALYSIS ABOUT WORN-OUT ON CONNECTING PIPE OF LOW-PRESSURE REHEATER FOR A BOILER OF 600 MW UNIT

BURST ANALYSIS OF HIGH TEMPERATURE RE-HEATER PIPE OF POWERSTATION

Residual Life Assessment on the Reformer Tube Welded with Serviced and New HP.Nb Material

Evaluating Fitness-for-Service of Corroded Metal Pipelines: Structural Reliability Bases

Comprehensive analysis of corrosion failure of blast furnace gas pipeline in a steel plant

FRACTURE ANALYSIS OF THE PIPES FOR EXCHANGING BOILER'S SURPLUS HEAT

Study on performance degradation of main steam pipe of X20CrMoV12.1 steel for long-term service

Residual Life Assessment of X20CrMoV12.1 Straight Main Steam Pipe in Service

Study on low cycle fatigue of ferritic-martensitic steel at high temperature

Failure Analysis and Fitness-for-service Assessment for a Pipeline

Failure Analysis of High-Temperature Reformer Tube of Incoloy 800H in Synthetic Ammonia Installation

RESIDUE LIFE PREDICTION AND RAPID MAINTENANCE STRATEGIES OF REFORMER FURNACE TUBES