Abstract:The physical and optical properties of thin films strongly depend on the film deposition techniques. In this research, Cu 2 ZnSnS 4 (CZTS) thin films were prepared using the sol–gel method and deposited on three kinds of substrates (glass, indium-doped tin oxide (ITO), and fluorine-doped tin oxide (FTO)) by the simple spray pyrolysis method. The influence of the substrate and Cu concentration (0.1 and 0.07 mol/L) on the physical properties of the prepared thin films was examined. The study of X-ray diffraction (XRD) investigation showed that all CZTS thin films possess a single-phase kesterite crystal structure. Field emission scanning electron microscopy (FE-SEM) images showed that the surface of the films was uniform, dense, and had almost no voids, and the particle size of the prepared thin film with the substrate (ITO) was larger than the other samples. The prepared films exhibited an optical band gap ranging from 2 to 2.4 eV. The lowest and highest values of the optical gap correspond to the film with the substrate (ITO) having a lower Cu concentration and the prepared film with the glass substrate having a higher Cu concentration, respectively. The electrical properties and sheet resistance of CZTS thin films were investigated. The best results in terms of electrical properties were related to the ITO substrate with a Cu concentration of 0.1 mol/L. A photoluminescence study showed that the strongest emission peak in the 700–800 nm region was observed for CZTS thin film on ITO substrate. Obtained results indicating the possibility of using the CZTS thin films for efficient and low-cost solar cell and optical applications. Our findings demonstrate that ITO serves as a superior substrate for CZTS fabrication at room temperature. Our results provide an overview of the feasibility of manufacturing optoelectronic devices based on CZTS thin film. Substrate selection is critical in many applications.

Single-step Preparation and Characterization of Cu2ZnSn(SxSe1−x)4 Thin Films Deposited by Pulsed Laser Deposition Method

Investigation on in-situ thermal treatment of room-temperature pulsed laser deposition technique: How to improve Cu2ZnSnS4 films for photoelectric application without sulfurization

Composition Dependence of Structure and Optical Properties of Cu2ZnSn(S,Se)4 Solid Solutions: an Experimental Study

Optoeletronic investigation of Cu 2 ZnSn(S,Se) 4 thin-films & Cu 2 ZnSn(S,Se) 4 /CdS interface with scanning probe microscopy

Preparation And Characterization Of Cu2znsns4 Thin Films And Solar Cells Fabricated From Quaternary Cu-Zn-Sn-S Target

CTZS Thin Films Grown by a Sequential Deposition of Precursors

Facile growth of Cu2ZnSn(SSe)4 thin films with controlled phase and microstructure evolution from green ethanol-based molecular solutions

Using Cu–Zn–Sn–O Precursor to Optimize CZTSSe Thin Films Fabricated by Se Doping With CZTS Thin Films

High-sulfur Cu2ZnSn(S,Se)4 Films by Sulfurizing As-Deposited CZTSe Film: the Evolutions of Phase, Crystallinity and S/(S+Se) Ratio

Investigation into complex defect properties of near-stoichiometric Cu2ZnSnSe4 thin film

Substrate and Cu concentration-dependent physical properties of spray-deposited Cu2ZnSnS4 thin films: a comparative study

Polycrystalline ZnTe Thin Film on Silicon Synthesized by Pulsed Laser Deposition and Subsequent Pulsed Laser Melting

CZTSe solar cells prepared by electrodeposition of Cu/Sn/Zn stack layer followed by selenization at low Se pressure

Study of optical and structural properties of CZTS thin films using copper capping layer and sulfurization to correct stoichiometry.

Study on the Optimization of Cu-Zn-Sn-O to Prepare Cu2ZnSnS4 Thin Film via a Nano Ink Coating Method

Structural and optical properties of Cu2ZnSnSe4 nanocrystals thin film

Fabrication and Electrochemical Characterization of Copper Selenide Thin Films by Pulsed Laser Deposition

Deposition of nano-crystalline Cu2ZnSnS4 thin film in one step without sulfurization: Future prospects

Sb Doping Strategy to Promote Growth and Suppress Defects in Solution-Processed CZTSSe Solar Cells for Improved Optoelectronic Performance

Mapping the Energetics of Defect States in Cu2ZnSnS4 films and the Impact of Sb Doping

Band Positions and Photoelectrochemical Properties of Cu2znsns4 Thin Films by the Ultrasonic Spray Pyrolysis Method