Abstract:The physical and optical properties of thin films strongly depend on the film deposition techniques. In this research, Cu 2 ZnSnS 4 (CZTS) thin films were prepared using the sol–gel method and deposited on three kinds of substrates (glass, indium-doped tin oxide (ITO), and fluorine-doped tin oxide (FTO)) by the simple spray pyrolysis method. The influence of the substrate and Cu concentration (0.1 and 0.07 mol/L) on the physical properties of the prepared thin films was examined. The study of X-ray diffraction (XRD) investigation showed that all CZTS thin films possess a single-phase kesterite crystal structure. Field emission scanning electron microscopy (FE-SEM) images showed that the surface of the films was uniform, dense, and had almost no voids, and the particle size of the prepared thin film with the substrate (ITO) was larger than the other samples. The prepared films exhibited an optical band gap ranging from 2 to 2.4 eV. The lowest and highest values of the optical gap correspond to the film with the substrate (ITO) having a lower Cu concentration and the prepared film with the glass substrate having a higher Cu concentration, respectively. The electrical properties and sheet resistance of CZTS thin films were investigated. The best results in terms of electrical properties were related to the ITO substrate with a Cu concentration of 0.1 mol/L. A photoluminescence study showed that the strongest emission peak in the 700–800 nm region was observed for CZTS thin film on ITO substrate. Obtained results indicating the possibility of using the CZTS thin films for efficient and low-cost solar cell and optical applications. Our findings demonstrate that ITO serves as a superior substrate for CZTS fabrication at room temperature. Our results provide an overview of the feasibility of manufacturing optoelectronic devices based on CZTS thin film. Substrate selection is critical in many applications.

Substrate and Cu concentration-dependent physical properties of spray-deposited Cu2ZnSnS4 thin films: a comparative study

Synthesis and characterization of CZTS and Cu2-xAgxZnSnS4 thin films for the application of solar cells

Band Positions and Photoelectrochemical Properties of Cu2znsns4 Thin Films by the Ultrasonic Spray Pyrolysis Method

Synthesis and Characterization of Cu 2 ZnSnS 4 from Cu 2 SnS 3 and ZnS Compounds

The photovoltaic properties of novel narrow band gap Cu2SnS3 films prepared by a spray pyrolysis method

Influence of Sulfurization Temperature on Physical Properties of Cu2znsns4 Thin Films

Optical and structural investigation of ZnS:Cu thin films synthesized by spray pyrolysis

Reaction Time and Film Thickness Effects on Phase Formation and Optical Properties of Solution Processed Cu2ZnSnS4 Thin Films

An Investigation on Structural, Morphological, Optical, and Electrical Properties of Copper Zinc Tin Sulfide (CZTS) Thin Films Prepared by SILAR Method

Deposition of nano-crystalline Cu2ZnSnS4 thin film in one step without sulfurization: Future prospects

CuS p- type thin film characterization deposited on Ti, ITO and glass substrates using spray pyrolysis deposition (SPD) for light emitting diode (LED) application

Study on the Optimization of Cu-Zn-Sn-O to Prepare Cu2ZnSnS4 Thin Film via a Nano Ink Coating Method

Study of optical and structural properties of CZTS thin films using copper capping layer and sulfurization to correct stoichiometry.

CTZS Thin Films Grown by a Sequential Deposition of Precursors

Structural and Optical Properties of the Cu2znsnse4 Thin Films Grown by Nano-Ink Coating and Selenization

Investigation of nucleation and growth mechanism of Cu2ZnSnS4 absorber layer electrodeposition on Indium Tin Oxide coated glass

Manufacture of different oxides with high uniformity for copper zinc tin sulfide (CZTS) based solar cells

Preparation And Characterization Of Cu2znsns4 Thin Films And Solar Cells Fabricated From Quaternary Cu-Zn-Sn-S Target

Application of Taguchi method to optimize the sol–gel dip-coating process of the semiconductor Cu2ZnSnS4 with good optical properties

Optical and Electrical Properties Study of Sol-Gel Derived Cu2znsns4 Thin Films for Solar Cells

Impact of Sol–gel Precursor Treatment with Preheating Temperature on Properties of Cu2ZnSnS4 Thin Film and Its Photovoltaic Solar Cell