Abstract:High-quality ZnO films were grown on Si(1 0 0) substrates with low-temperature (LT) ZnO buffer layers by an electron cyclotron resonance (ECR)-assisted molecular-beam epitaxy (MBE). In order to investigate the optimized buffer layer temperature, ZnO buffer layers of about 1.1 μm were grown at different growth temperatures of 350, 450 and 550 °C, followed by identical high-temperature (HT) ZnO films with the thickness of 0.7 μm at 550 °C. A ZnO buffer layer with a growth temperature of 450 °C (450 °C-buffer sample) was found to greatly enhance the crystalline quality of the top ZnO film compared to others. The root mean square (RMS) roughness (3.3 nm) of its surface is the smallest, compared to the 350 °C-buffer sample (6.7 nm), the 550 °C-buffer sample (7.4 nm), and the sample without a buffer layer (6.8 nm). X-ray diffraction (XRD), photoluminescence (PL) and Raman scattering measurements were carried out on these samples at room temperature (RT) in order to characterize the crystalline quality of ZnO films. The preferential c-axis orientations of (0 0 2) ZnO were observed in the XRD spectra. The full-width at half-maximum (FWHM) value of the 450 °C-buffer sample was the narrowest as 0.209°, which indicated that the ZnO film with a buffer layer grown at this temperature was better for the subsequent ZnO growth at elevated temperature of 550 °C. Consistent with these results, the 450 °C-buffer sample exhibits the highest intensity and the smallest FWHM (130 meV) of the ultraviolet (UV) emission at 375 nm in the PL spectrum. The ZnO characteristic peak at 438.6 cm−1 was found in Raman scattering spectra for all films with buffers, which is corresponding to the E2 mode.

Effect of Mgo in Zno Films Grown on Nitrided Sapphires

Structural and Optical Studies of Mg(X)Zn(1-X)Ofilms Grown on Sapphire

The Effects of Oxygen Partial Pressure and Substrate Temperature on the Structural and Optical Properties of Zno Films

Effect of Magnesium Doping on the Light-Induced Hydrophilicity of Zno Thin Films

Preparation and Characterization of Mg-doped ZnO Thin Films by Sol–gel Method

Tri-Buffer Process: A New Approach to Obtain High-Quality Zno Epitaxial Films on Sapphire Substrates

Effects of Post-Annealing Treatment on the Structural and Optical Properties of Cubic Mg Chi Zn1-Chi O Thin Films Grown on Sapphire

Effect of the ZnO buffer layer thickness on AZO film properties

ZnO growth on Si with low-temperature CdO and ZnO buffer layers by molecular-beam epitaxy

Epitaxial Growth Of Zno On Gan/Sapphire Substrate By Radio-Frequency Magnetron Sputtering

MBE‐grown ZnO Film on Sapphire Substrate with Double Buffer Layers

Molecular Beam Epitaxy Growth of Single-Domain and High-Quality ZnO Layers on Nitrided (0001) Sapphire Surface

Effect of Growth and Annealing on ZnO Buffer by MOCVD

Growth of high quality Zn0.9Mg0.1O films on c-plane sapphire substrates by plasma-assisted molecular beam epitaxy

Effect of Mg Content and Buffer Layer on Properties of ZnMgO: Ga Thin Films

Preparation of Mgo Thin-Films by Dual-Ion Beam Sputtering

Growth of Non-Polar Zn1−x Mg X O Thin Films with Different Mg Contents on R-Plane Sapphire Substrates by Plasma-Assisted Molecular Beam Epitaxy

Surface morphology of ZnO buffer layer and its effects on the growth of GaN films on Si substrates by magnetron sputtering

The effect of Mg doping concentration and annealing on the structure and luminescence properties of ZnO thin films

Structural Characterization of Zn-polar ZnO Films Grown on Mg-modified C-Al2o3 (0001) Surface

ZnO Growth on Si with Low-Temperature ZnO Buffer Layers by ECR-assisted MBE