Abstract:Magnesium oxide (MgO) thin films with different magnesium concentrations ([Mg2+] = 0.05, 0.1, 0.15 and 0.2 mol·L−1) in a spray solution have been successfully grown using a spray pyrolysis technique. X-ray diffraction (XRD), Maud software, FTIR spectroscopy, a confocal microscope, Wien2k software, spectrophotometry and a Photoluminescence spectrometer were used to investigate the structural, morphological and optical properties. XRD analysis revealed a better crystalline quality of the MgO thin layer synthesized with [Mg2+] = 0.15 mol·L−1, which crystallized into a face-centered cubic structure along the preferred orientation (200) lattice plan. The enhancement of the crystalline quality for the MgO thin film ([Mg2+] = 0.15 mol·L−1) was obtained, which was accompanied by an increment of 94.3 nm of the crystallite size. No secondary phase was detected and the purity phase of the MgO thin film was confirmed using Maud software. From the transmission spectra results, high transparent and antireflective properties of the MgO thin film were observed, with an average transmission value of about 91.48% in the visible range, which can be used as an optical window or buffer layer in solar cell applications. The films also have a high reflectance value in the IR range, which indicates that the highly reflective surface will prevent an increase in surface temperature under solar irradiation, which could be beneficial in solar cell applications. A direct band gap type was estimated using the Tauc relation which is close to the experimental value of 4.0 eV for optimal growth. The MgO material was tested for the degradation of methylene blue (MB), which reached a high photodegradation rate of about 83% after 180 min under sunlight illumination. These experimental trends open a new door for promising the removal of water contaminants for photocatalysis application.

Preparation of Mgo Thin-Films by Dual-Ion Beam Sputtering

Preparation of MgO Thin Films by Dual Ion Beam Sputtering

Preparation and Characterization of Mg-doped ZnO Thin Films by Sol–gel Method

Heteroepitaxial Growth of MgO Films by Dual Ion Beam Sputtering

Structural and Optical Studies of Mg(X)Zn(1-X)Ofilms Grown on Sapphire

MBE Preparation and Characterization of ZnO Thin Film

GROWTH OF MgO THIN FILMS ON Si SUBSTRATES BY MAGNETRON SPUTTERING

Applications of Cubic MgZnO Thin Films in Metal–Insulator–Silicon Structures

Growth of Cubic MgxZn1-xO Films and Characterization

Effect of Mg Content and Buffer Layer on Properties of ZnMgO: Ga Thin Films

The Study of Composition Non-Uniformity in Ternary Mgxzn1-Xo Thin Films

Low Voltage Ion Plating Technique for the Deposition of ZnS, MgF2 Films

Structural, Electrical And Optical Properties Of Zn1-Xmgxo Films Prepared By Reactive Dc Sputtering

Effect of Mgo in Zno Films Grown on Nitrided Sapphires

Structural, morphological, optical and electrical characterization of MgO thin films grown by sputtering technique on different substrates

Surface morphology of ZnO buffer layer and its effects on the growth of GaN films on Si substrates by magnetron sputtering

Synthesis of β-Ga2O3:Mg Thin Films by Electron Beam Evaporation and Postannealing

Synthesis and Characterization of MgO Thin Films Obtained by Spray Technique for Optoelectronic Applications

Conformal MgO film grown at high rate at low temperature by forward-directed chemical vapor deposition

Synthesis of Mg and Zn diolates and their use in metal oxide deposition

Epitaxial Mg2SiO4 Thin Films with a Spinel Structure Grown on Si Substrates